Weldability of 1000 MPa Grade Ultra-low Carbon Bainitic Steel

Maximum hardness test in weld heat-affected zone (HAZ), oblique Y-groove cracking test and mechanical property test of welding joint of 1000 MPa grade ultra-low carbon bainitic steel were carried out, so as to research the weldability of the steel. The results show that the steel has lower cold cracking sensitivity, and preheating temperature of 100 degrees C can help completely eliminate cold cracks, generating good process weldability. The increase of preheating temperature can reduce the hardening degree of heat-affected zone. The strength of welding joint decreases and hardness reduces when heat inputs increase, and excellent mechanical properties can be obtained when low welding heat inputs are used. Fine lath bainites of different orientations combined with a few granular bainites that effectively split the original coarse austenite grains are the foundation of good properties.