Plasma-Nitriding Properties of CoCrFeMnNi High-Entropy Alloys Produced by Spark Plasma Sintering

High-entropy alloys (HEAs) were fabricated by powder metallurgy using gas-atomized powder and spark plasma sintering (SPS) followed by surface modification (plasma nitriding) of the sintered sample. Plasma nitriding forms nitride and induces solid-soluting of N; it enables the diffusion of N atoms by removing the passive film formed on the surface of alloys such as stainless steel, Al alloys, and Ti alloys, via the sputtering of cations during glow discharge. Therefore, plasma nitriding has the potential to process HEAs that contain strong oxidizing elements such as Cr, Al, and Ti. In this work, a sintered CoCrFeMnNi HEA was plasma-nitrided and its properties were subsequently evaluated. A uniform microstructure without segregation was obtained in the SPS sample, and its hardness and wear resistance were found to have improved. Analysis of the sample surface after nitriding revealed that an expanded face-centered cubic phase formed on the surface plasma-nitrided at 673 K and that a CrN phase formed on the surface plasma-nitrided at temperatures greater than 723 K. The surface hardness of the plasma-nitrided sample was 1200 HV or greater, and the wear resistance and pitting corrosion resistance were improved compared with those of the untreated sample.