Corrosion stability of polyester coatings on steel pretreated with different iron-phosphate coatings

被引:19
作者
Jegdic, B. V. [1 ]
Bajat, J. B. [2 ]
Popic, J. P. [3 ]
Miskovic-Stankovic, V. B. [2 ]
机构
[1] Inst GOSA, Belgrade 11000, Serbia
[2] Univ Belgrade, Fac Technol & Met, Belgrade 11120, Serbia
[3] ICTM IEC, Belgrade 11001, Serbia
关键词
Corrosion; Electrochemical impedance spectroscopy; Adhesion; AFM; Polyester coating; Steel; ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY; ADHESION;
D O I
10.1016/j.porgcoat.2010.11.004
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
The influence of steel surface pretreatment with different types of iron-phosphate coatings on the corrosion stability and adhesion characteristics of polyester coatings on steel was investigated. The phosphate coating was chemically deposited either from the simple novel plating bath, or with the addition of NaNO2, as an accelerator in the plating bath. The morphology of phosphate coatings was investigated using atomic force microscopy (AFM). The corrosion stability of polyester coatings on steel pretreated by iron-phosphate coatings was investigated by electrochemical impedance spectroscopy (EIS) in 3% NaCl solution, while "dry" and "wet" adhesion were measured by a direct pull-off standardized procedure. It was shown that greater values of pore resistance. R-p, and smaller values of coating capacitance of polyester coating, C-c, on steel pretreated with iron-phosphate coating were obtained, as compared to polyester coating on steel phosphated with accelerator, and on the bare steel. The surface roughness of phosphate coating deposited on steel from the bath without accelerator is favorable in forming stronger bonds with polyester coating. Namely, the dry and wet adhesion measurements are in accordance with EIS measurements in 3% NaCl solution, i.e. lower adhesion values were obtained for polyester coating on steel phosphated with accelerator and on the bare steel, while the iron-phosphate pretreatment from the novel bath enhanced the adhesion of polyester coating on steel. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码:127 / 133
页数:7
相关论文
共 23 条
[1]   Corrosion mechanisms of phosphated zinc layers on steel as substrates for automotive coatings [J].
Amirudin, A ;
Thierry, D .
PROGRESS IN ORGANIC COATINGS, 1996, 28 (01) :59-75
[2]  
[Anonymous], METAL FINISHING
[3]   Adhesion characteristics and corrosion stability of epoxy coatings electrodeposited on phosphated hot-dip galvanized steel [J].
Bajat, J. B. ;
Miskovic-Stankovic, V. B. ;
Popic, J. P. ;
Drazic, D. M. .
PROGRESS IN ORGANIC COATINGS, 2008, 63 (02) :201-208
[4]   Corrosion protection of aluminium pretreated by vinyltriethoxysilane in sodium chloride solution [J].
Bajat, J. B. ;
Milosev, I. ;
Jovanovic, Z. ;
Jancic-Heinemann, R. M. ;
Dimitrijevic, M. ;
Miskovic-Stankovic, V. B. .
CORROSION SCIENCE, 2010, 52 (03) :1060-1069
[5]   Protective properties of epoxy coatings electrodeposited on steel electrochemically modified by Zn-Ni alloys [J].
Bajat, JB ;
Miskovic-Stankovic, VB .
PROGRESS IN ORGANIC COATINGS, 2004, 49 (03) :183-196
[6]   Electrochemical deposition and characterization of Zn-Co alloys and corrosion protection by electrodeposited epoxy coating on Zn-Co alloy [J].
Bajat, JB ;
Miskovic-Stankovic, VB ;
Maksimovic, MD ;
Drazic, DM ;
Zec, S .
ELECTROCHIMICA ACTA, 2002, 47 (25) :4101-4112
[7]   The effects of niobium and nickel on the corrosion resistance of the zinc phosphate layers [J].
Banczek, E. P. ;
Rodrigues, P. R. P. ;
Costa, I. .
SURFACE & COATINGS TECHNOLOGY, 2008, 202 (10) :2008-2014
[8]   Investigation on the effect of benzotriazole on the phosphating of carbon steel [J].
Banczek, E. P. ;
Rodrigues, P. R. P. ;
Costa, I. .
SURFACE & COATINGS TECHNOLOGY, 2006, 201 (06) :3701-3708
[9]  
BIESTEK T, 1976, ELECTROLYTIC CHEM CO, P180
[10]   Electrochemical impedance spectroscopy and linear polarization applied to evaluation of porosity of phosphate conversion coatings on electrogalvanized steels [J].
de Freitas Cunha Lins, Vanessa ;
de Andrade Reis, Geraldo Francisco ;
de Araujo, Carlos Roberto ;
Matencio, Tulio .
APPLIED SURFACE SCIENCE, 2006, 253 (05) :2875-2884