Investigation of Process Parameters of Phosphogypsum for Preparing Calcium Sulfoaluminate Cement

被引:6
|
作者
Zhang, Ping [1 ]
Zhang, Bingxin [1 ]
Chang, Jun [2 ]
Wang, Tong [2 ]
Zhang, Jixin [2 ]
Li, Li [3 ]
机构
[1] Guizhou Normal Univ, Sch Mat & Architectural Engn, Guiyang 550025, Peoples R China
[2] Dalian Univ Technol, Sch Civil Engn, Dalian 116024, Peoples R China
[3] Northwest A&F Univ, Coll Water Resources & Architectural Engn, Xianyang 712100, Peoples R China
基金
中国国家自然科学基金;
关键词
phosphogypsum; calcium sulfoaluminate cement; calcination temperature; calcination time; compressive strength; HYDRATION; SYSTEM; GYPSUM;
D O I
10.3390/buildings12111774
中图分类号
TU [建筑科学];
学科分类号
0813 ;
摘要
Preparing calcium sulfoaluminate cement (CAS) from solid waste phosphogypsum (PG) instead of natural gypsum is an effective way to utilize solid waste. In this paper, CAS clinker was successfully prepared from PG and the mineral content of calcium sulfoaluminate (C(4)A(3)(S) over bar) in the sample was above 65%. The effects of raw material ratio, calcination temperature, and time on clinker composition were investigated. The mechanical properties of different samples were tested. The optimum ratio for preparing CAS using PG was 42.23% limestone, 17.43% PG, and 40.34% bauxite. The optimal calcination conditions are a high temperature of 1250 degrees C for 45 min. The 3-day compressive strengths of the laboratory-prepared CAS were all above 50 MPa. It was found that as the calcination temperature increased, the amount of C(4)A(3)(S) over bar produced gradually increased. Temperatures above 1300 degrees C resulted in the decomposition of C(4)A(3)(S) over bar. The calcination time did not significantly affect the mineral composition of the clinker or the strength of the cement. C(4)A(3)(S) over bar was observed to be rounded and hexagonal platelets with crystal sizes of 1 to 2 mu m, a relatively small size that is favorable to the hydration of C(4)A(3)(S) over bar, as observed by SEM images. In addition, the high calcination temperature affected the particle morphology of C(4)A(3)(S) over bar, changing it from a well-defined polygonal structure to a molten state. The test results provide helpful information for improving PG utilization and applying PG in CAS production.
引用
收藏
页数:17
相关论文
共 50 条
  • [21] A New Belitic Calcium Sulfoaluminate Cement
    Deo, Omkar
    Bhuskute, Neel
    Paniagua, Julio
    Guijosa, Javier
    Rivera, Janeth
    Bescher, Eric P.
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2023, 35 (11)
  • [22] Utilisation of phosphogypsum for sulfate-rich belite sulfoaluminate cement production
    Shen, Yan
    Qian, Jueshi
    ADVANCES IN CEMENT RESEARCH, 2015, 27 (09) : 515 - 525
  • [23] HIGH-TEMPERATURE SYNTHESIS OF CALCIUM SULFOALUMINATE FROM PHOSPHOGYPSUM
    VALENTI, G
    SANTORO, L
    GAROFANO, R
    THERMOCHIMICA ACTA, 1987, 113 : 269 - 275
  • [24] Microstructural Evolution of Calcium Sulfoaluminate Cement during the Wet-Carbonation Process
    Zhang, Yangyang
    Yang, Hang
    Zhang, Qunli
    Qian, Quan
    Zhang, Chengwei
    Wu, Kai
    Shen, Peiliang
    BUILDINGS, 2024, 14 (02)
  • [25] Effect of different retarders on setting time and mechanical properties of hemihydrate phosphogypsum-calcium sulfoaluminate cement composite binder
    Jin, Zihao
    Wang, Liyue
    Su, Ying
    He, Xingyang
    Ma, Baoguo
    Wang, Yingbin
    Li, Yubo
    Qi, Huahui
    Wang, Bin
    CONSTRUCTION AND BUILDING MATERIALS, 2024, 411
  • [26] EFFECT OF BORAX ON CALCIUM SULFOALUMINATE CEMENT PROPERTIES
    Shen, Yan
    Zhang, Wei
    Zhu, Hangyu
    LI, Jiang
    Shi, Shoufen
    CERAMICS-SILIKATY, 2023, 67 (01) : 10 - 19
  • [27] Advances in clinkering technology of calcium sulfoaluminate cement
    Galan, Isabel
    Elhoweris, Ammar
    Hanein, Theodore
    Bannerman, Marcus N.
    Glasser, Fredrik P.
    ADVANCES IN CEMENT RESEARCH, 2017, 29 (10) : 405 - 417
  • [28] Pore solution composition of calcium sulfoaluminate cement
    Andac, M
    Glasser, FP
    ADVANCES IN CEMENT RESEARCH, 1999, 11 (01) : 23 - 26
  • [29] Belite-calcium sulfoaluminate cement prepared with phosphogypsum: Influence of P2O5 and F on the clinker formation and cement performances
    Huang, Yongbo
    Qian, Jueshi
    Kang, Xiaojuan
    Yu, Jincheng
    Fan, Yingru
    Dang, Yudong
    Zhang, Wensheng
    Wang, Shoude
    CONSTRUCTION AND BUILDING MATERIALS, 2019, 203 : 432 - 442
  • [30] Pore solution composition of calcium sulfoaluminate cement
    Univ of Aberdeen, Aberdeen, United Kingdom
    Adv Cem Res, 1 (23-26):