High trapped fields in bulk YBa2Cu3O7-delta samples at temperatures around 50 K

被引：42

作者：

Fuchs, G

Krabbes, G

Schatzle, P

Gruss, S

Stoye, P

Staiger, T

Muller, KH

Fink, J

Schultz, L

机构：

[1] Inst. F. Festkorper- W., D-01171 Dresden

来源：

APPLIED PHYSICS LETTERS | 1997年 / 70卷 / 01期

关键词：

D O I：

10.1063/1.119280

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Bulk melt textured YBa2Cu3O7-delta samples with single grains of about 24 mm diameter were obtained by use of SmBa2Cu3O7-x seed crystals. The maximum trapped field B-0 in the gap between two samples was investigated as function of temperature. B-0 increased from 1 T at 77 K to 8.5 T at 51.5 K, which is the highest trapped field achieved in nonirradiated samples. At low temperatures, cracking of the samples was observed under magnetic pressure. In this temperature range, the trapped field is limited by the mechanical strength of the samples, for which a value of 25 MPa was estimated. (C) 1997 American Institute of Physics.

引用

页码：117 / 119

页数：3

共 12 条

[1] MAGNETIZATION OF HARD SUPERCONDUCTORS [J].

BEAN, CP .

PHYSICAL REVIEW LETTERS, 1962, 8 (06) :250-+

[2] THERMAL FLUCTUATIONS OF VORTEX LINES, PINNING, AND CREEP IN HIGH-TC SUPERCONDUCTORS [J].

FEIGELMAN, MV ;

VINOKUR, VM .

PHYSICAL REVIEW B, 1990, 41 (13) :8986-8990

[3]

GAWALEK W, 1994, APPL SUPERCOND, V2, P465

[4] MODIFIED MELT TEXTURING PROCESS FOR YBCO BASED ON THE POLYTHERMIC SECTION YO1.5-BA0.4CU0.6O IN THE Y-BA-CU-O PHASE-DIAGRAM AT 0.21 BAR OXYGEN-PRESSURE [J].

KRABBES, G ;

SCHATZLE, P ;

BIEGER, W ;

WIESNER, U ;

STOVER, G ;

WU, M ;

STRASSER, T ;

KOHLER, A ;

LITZKENDORF, D ;

FISCHER, K ;

GORNERT, P .

PHYSICA C, 1995, 244 (1-2) :145-152

[5] MELT TEXTURING OF PREFERENTIALLY ALIGNED YBA2CU3OX SUPERCONDUCTOR BY A SEEDED DIRECTIONAL SOLIDIFICATION METHOD [J].

LEE, DF ;

PARTSINEVELOS, CS ;

PRESSWOOD, RG ;

SALAMA, K .

JOURNAL OF APPLIED PHYSICS, 1994, 76 (01) :603-605

[6]

LIU J, 1995, UNPUB P 1995 INT WOR, P353

[7] DAMAGE CAUSED BY MAGNETIC PRESSURE AT HIGH TRAPPED FIELD IN QUASI-PERMANENT MAGNETS COMPOSED OF MELT-TEXTURED Y-BA-CU-O SUPERCONDUCTOR [J].

REN, Y ;

WEINSTEIN, R ;

LIU, J ;

SAWH, RP ;

FOSTER, C .

PHYSICA C, 1995, 251 (1-2) :15-26

[8]

SCHATZLE P, 1995, APPL SUPERCOND, V1, P155

[9] EFFECT OF FLUX-CREEP ON THE TEMPERATURE-DEPENDENCE OF THE CURRENT-DENSITY IN Y-BA-CU-O CRYSTALS [J].

THOMPSON, JR ;

SUN, YR ;

CIVALE, L ;

MALOZEMOFF, AP ;

MCELFRESH, MW ;

MARWICK, AD ;

HOLTZBERG, F .

PHYSICAL REVIEW B, 1993, 47 (21) :14440-14447

[10] PERMANENT-MAGNETS OF HIGH-TC SUPERCONDUCTORS [J].

WEINSTEIN, R ;

CHEN, IG ;

LIU, J ;

XU, J ;

OBOT, V ;

FOSTER, C .

JOURNAL OF APPLIED PHYSICS, 1993, 73 (10) :6533-6535

← 1 2 →