Modes of flip chip solder joints under high electric current stressing

被引：0
作者：
Ye, H [1 ]
Basaran, C [1 ]
Hopkins, DC [1 ]
机构：
[1] SUNY Buffalo, UB Elect Packaging Lab, Buffalo, NY 14260 USA
来源：
2003 INTERNATIONAL SYMPOSIUM ON MICROELECTRONICS | 2003年 / 5288卷
关键词：
failure modes; flip chip; solder joint; electromigration; thermomigration; current stressing;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The failure modes of flip chip solder joints under current stressing are analyzed based on the experiments of 19 flip chip modules. Three different failure modes were reported. Among them, only Mode 3 failure is caused by the combined effect of electromigration and thermomigration, where void nucleation and growth contribute to the ultimate failure of the module. The void nucleation and growth in solder joint during current stressing is discussed in detail. The Ni UBM-solder interface is found to be the favorite site of voids nucleation and growth. The effect of pre-existing voids on the failure process of a solder joint is found to be dependent on their location.
引用
收藏
页码：801 / 806
页数：6
相关论文
共 50 条
  • [31] Secondary current crowding effect during electromigration of flip-chip solder joints
    Jang, J. W.
    Ramanathan, L. N.
    Tang, J.
    Frear, D. R.
    JOURNAL OF ELECTRONIC MATERIALS, 2008, 37 (02) : 185 - 188
  • [32] Secondary Current Crowding Effect during Electromigration of Flip-Chip Solder Joints
    J.W. Jang
    L.N. Ramanathan
    J. Tang
    D.R. Frear
    Journal of Electronic Materials, 2008, 37 : 185 - 188
  • [33] Influence of microstructure inhomogeneity on the electromigration behavior of flip chip solder joints
    Wang Sansan
    Wang Ying
    Zhang Ping
    Guo Lei
    Qin Hongbo
    Jiang Hongjie
    Yan Hong
    2016 17TH INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY (ICEPT), 2016, : 283 - 288
  • [34] Local melting induced by electromigration in flip-chip solder joints
    C. M. Tsai
    Y. L. Lin
    J. Y. Tsai
    Yi-Shao Lai
    C. R. Kao
    Journal of Electronic Materials, 2006, 35 : 1005 - 1009
  • [35] Computational analysis of the interfacial effect on electromigration in flip chip solder joints
    Kim, Dongchoul
    MICROELECTRONIC ENGINEERING, 2009, 86 (10) : 2132 - 2137
  • [36] Mesomechanical modelling of SnAgCu solder joints in flip chip
    Gong, Jicheng
    Liu, Changqing
    Conway, Paul P.
    Silberschmidt, Vadirn V.
    COMPUTATIONAL MATERIALS SCIENCE, 2008, 43 (01) : 199 - 211
  • [37] The Growth and Segregation of Intermetallic Compounds in the Bulk of Flip Chip Sn2.4Ag Solder Joint under Electrical Current Stressing
    Wang, Wei-Chieh
    Lin, Kwang-Lung
    Chiu, Ying-Ta
    Lai, Yi-Shao
    2013 IEEE 63RD ELECTRONIC COMPONENTS AND TECHNOLOGY CONFERENCE (ECTC), 2013, : 1600 - 1605
  • [38] Local melting induced by electromigration in flip-chip solder joints
    Tsai, C. M.
    Lin, Y. L.
    Tsai, J. Y.
    Lai, Yi-Shao
    Kao, C. R.
    JOURNAL OF ELECTRONIC MATERIALS, 2006, 35 (05) : 1005 - 1009
  • [39] Effect of UBM thickness on the mean time to failure of flip-chip solder joints under electromigration
    Lin, Y. L.
    Lai, Y. S.
    Lin, Y. W.
    Kao, C. R.
    JOURNAL OF ELECTRONIC MATERIALS, 2008, 37 (01) : 96 - 101
  • [40] Effect of UBM Thickness on the Mean Time to Failure of Flip-Chip Solder Joints under Electromigration
    Y.L. Lin
    Y.S. Lai
    Y.W. Lin
    C.R. Kao
    Journal of Electronic Materials, 2008, 37 : 96 - 101
12345