Microstructure and mechanical properties of X80 pipeline steels in different cooling schedules

被引：8
作者：
Zhou, Min [1 ]
Du, Linxiu [1 ]
Liu, Xianghua [1 ]
机构：
[1] Northeastern Univ, State Key Lab Rolling Technol & Automat, Shenyang 110819, Peoples R China
来源：
ACTA METALLURGICA SINICA-ENGLISH LETTERS | 2010年 / 23卷 / 03期
关键词：
Microstructure; Mechanical properties; Cooling schedule; Relaxation; TRANSITION-TEMPERATURE REGION; FRACTURE-TOUGHNESS ANALYSIS; MICROALLOYED STEELS; X70;
D O I：
10.11890/1006-7191-103-171
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The microstructures and mechanical properties of three X80 pipeline steel plates were investigated in this study. The plates were hot rolled by two stages, and cooled by three different cooling schedules to obtain different microstructures and mechanical properties. Transmission electron microscope (TEM) was used to observe the microstructure., The results indicated that the amount of polygonal ferrite (PF) and quasi-polygonal ferrite (QPF) decreased with decreasing of the finish cooling temperature (FCT), while the amount and size of M-A islands were larger. Relaxation promoted the Charpy V-notch (CVN) impact toughness at -20 degrees C, but not the drop weight tear testing (DWTT) property at -15 degrees C, and decreased the strength of the steel.
引用
收藏
页码：171 / 175
页数：5
相关论文
共 10 条
[1]   Effect of microstructure on the yield ratio and low temperature toughness of linepipe steels [J].
Kim, YM ;
Kim, SK ;
Lim, YJ ;
Kim, NJ .
ISIJ INTERNATIONAL, 2002, 42 (12) :1571-1577
[2]   Continuous cooling transformation behaviour of high strength microalloyed steels for linepipe applications [J].
Manohar, PA ;
Chandra, T .
ISIJ INTERNATIONAL, 1998, 38 (07) :766-774
[3]   On the processing of Fe-C-Mn-Nb steels to produce plates for pipelines with sour gas resistance [J].
Mendoza, R ;
Alanis, M ;
Perez, R ;
Alvarez, O ;
Gonzalez, C ;
Juarez-Islas, JA .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 337 (1-2) :115-120
[4]  
Ohtsuka H., 1988, THERMEC 88, P352
[5]   Effects of hot deformation and accelerated cooling on microstructural evolution of low carbon microalloyed steels [J].
Qu, JB ;
Shan, YY ;
Zhao, MC ;
Yang, H .
MATERIALS SCIENCE AND TECHNOLOGY, 2002, 18 (02) :145-150
[6]   Fracture toughness analysis in transition temperature region of API X70 pipeline steels [J].
Shin, Sang Yong ;
Hwang, Byoungchul ;
Kim, Sangho ;
Lee, Sunghak .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 429 (1-2) :196-204
[7]   Fracture-Toughness Analysis in Transition-Temperature Region of Three American Petroleum Institute X70 and X80 Pipeline Steels [J].
Shin, Sang Yong ;
Woo, Kuk Je ;
Hwang, Byoungchul ;
Kim, Sangho ;
Lee, Sunghak .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (04) :867-876
[8]   Transmission electron microscopy of martensite/austenite islands in pipeline steel X70 [J].
Wang, Chunming ;
Wu, Xingfang ;
Liu, Jie ;
Xu, Ning'an .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 438 (267-271) :267-271
[9]   Relation among rolling parameters, microstructures and mechanical properties in an acicular ferrite pipeline steel [J].
Wang, Wei ;
Yan, Wei ;
Zhu, Lin ;
Hu, Ping ;
Shan, Yiyin ;
Yang, Ke .
MATERIALS & DESIGN, 2009, 30 (09) :3436-3443
[10]   Challenge of mechanical properties of an acicular ferrite pipeline steel [J].
Xiao, Fu-Ren ;
Liao, Bo ;
Shan, Yi-Yin ;
Qiao, Gui-Ying ;
Zhong, Yong ;
Zhang, Chunling ;
Yang, Ke .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 431 (1-2) :41-52
1