Quantifying the effects of tempering on individual phase properties of DP980 steel with nanoindentation

被引：51
作者：
Cheng, G. [1 ]
Zhang, F. [2 ]
Ruimi, A. [3 ]
Field, D. P. [2 ]
Sun, X. [1 ]
机构：
[1] Pacific NW Natl Lab, Phys & Computat Sci Directorate, POB 999, Richland, WA 99352 USA
[2] Washington State Univ, Sch Mech & Mat Engn, Pullman, WA 99164 USA
[3] Texas A&M Univ, Dept Mech Engn, Doha, Qatar
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2016年 / 667卷
关键词：
Nanoindentation; Plastic flow properties; Tempering; DP steels; STRAIN GRADIENT PLASTICITY; MECHANICAL-PROPERTIES; DEFORMATION-BEHAVIOR; HARDENING BEHAVIOR; TENSILE PROPERTIES; HEAT-TREATMENT; MARTENSITE; FERRITE; STRENGTH; HARDNESS;
D O I：
10.1016/j.msea.2016.05.011
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Tempering treatment is conducted on a commercial dual phase (DP) 980 steel at 250 degrees C and 400 degrees C for 60 min each. Ferrite and martensite grains are distinguished using electron backscatter diffraction (EBSD) and scanning probe microscopy (SPM), and the martensite volume fractions (MVF) are determined based on the image quality (IQ) map. Indentation tests combined with a newly developed inverse method are used to obtain the individual phase flow properties in each sample. The results show that, i) tempering significantly reduces martensite yield strength, while it slightly reduces the ferrite yield strength; ii) tempering temperature has a more significant influence on the work hardening exponent of ferrite than that of martensite. As a validation, a simple rule-of-mixtures is used to verify the above-predicted individual phase flow stresses with the experimentally obtained overall true stress vs. true strain curves. (c) 2016 Elsevier B.V. All rights reserved.
引用
收藏
页码：240 / 249
页数：10
相关论文
共 56 条
[1]  
[Anonymous], 2015, MATH PROBL ENG
[2]   Tempering of Martensite in Dual-Phase Steels and Its Effects on Softening Behavior [J].
Baltazar Hernandez, V. H. ;
Nayak, S. S. ;
Zhou, Y. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (10) :3115-3129
[3]   Nanoindentation and microstructure analysis of resistance spot welded dual phase steel [J].
Baltazar Hernandez, V. H. ;
Panda, S. K. ;
Kuntz, M. L. ;
Zhou, Y. .
MATERIALS LETTERS, 2010, 64 (02) :207-210
[4]  
Bhattacharya D, 2005, JOINT INT C HSLA STE, P70
[5]   The relationship between hardness and yield stress in irradiated austenitic and ferritic steels [J].
Busby, JT ;
Hash, MC ;
Was, GS .
JOURNAL OF NUCLEAR MATERIALS, 2005, 336 (2-3) :267-278
[6]   Orientation gradients and geometrically necessary dislocations in ultrafine grained dual-phase steels studied by 2D and 3D EBSD [J].
Calcagnotto, Marion ;
Ponge, Dirk ;
Demir, Eralp ;
Raabe, Dierk .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (10-11) :2738-2746
[7]   TEMPER-AGING OF CONTINUOUSLY ANNEALED LOW-CARBON DUAL PHASE STEEL [J].
CHANG, PH .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (01) :73-86
[8]   Determining individual phase properties in a multi-phase Q&P steel using multi-scale indentation tests [J].
Cheng, G. ;
Choi, K. S. ;
Hu, X. ;
Sun, X. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 652 :384-395
[9]   Advanced Micromechanical Model for Transformation-Induced Plasticity Steels with Application of In-Situ High-Energy X-Ray Diffraction Method [J].
Choi, K. S. ;
Liu, W. N. ;
Sun, X. ;
Khaleel, M. A. ;
Ren, Y. ;
Wang, Y. D. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2008, 39A (13) :3089-3096
[10]   Determination of carbon distributions in quenched and partitioned microstructures using nanoscale secondary ion mass spectroscopy [J].
Choi, Kyoo Sil ;
Zhu, Zihua ;
Sun, Xin ;
De Moor, Emmanuel ;
Taylor, Mark D. ;
Speer, John G. ;
Matlock, David K. .
SCRIPTA MATERIALIA, 2015, 104 :79-82
123456