Optical method for evaluation of shrinkage in two dimensions during drying of ceramic green bodies

被引：12

作者：

Oummadi, Siham ^{[1
]}

Nait-Ali, Benoit ^{[1
]}

Alzina, Arnaud ^{[1
]}

Paya, Marie-Clotilde ^{[1
]}

Gaillard, Jean-Marie ^{[1
]}

Smith, David S. ^{[1
]}

机构：

[1] Univ Limoges, IRCER, CNRS, UMR 7315, 12 Rue Atlantis, F-87068 Limoges, France

来源：

OPEN CERAMICS | 2020年 / 2卷

关键词：

Drying; Shrinkage; Anisotropy; DIAMOND/SIC COMPOSITES; OXIDATION; FABRICATION; MICROSTRUCTURE; RESISTANCE; SURFACES; OXYGEN; HIP;

D O I：

10.1016/j.oceram.2020.100016

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The evolution of shrinkage and mass during drying of kaolin and alumina green bodies was characterized. Standard practise uses a position sensor with simultaneous mass measurement. In this work an optical method was developed to follow shrinkage in two orthogonal directions. Green body samples were made by pressing of ceramic pastes. Results have been compared through the well known Bigot curves which show two distinct stages. First a linear shrinkage with the evaporated water loss is observed. Then in the second stage with further water loss, negligible dimension changes occur. For each material, the overall shrinkage values are identical in the two directions parallel to the pressing axis, but higher in the pressing direction. This difference is related to the shaping method yielding a preferential orientation of grains. Anisotropy in shrinkage is more significant for kaolin with tabular shaped grains compared to the more isometric grains of alumina.

引用

页数：7

共 39 条

[1]

Adloff L., 2020, Master thesis

[2] VAPOR-PHASE OXIDATION OF DIAMOND SURFACES IN O2 STUDIED BY DIFFUSE-REFLECTANCE FOURIER-TRANSFORM INFRARED AND TEMPERATURE-PROGRAMMED DESORPTION SPECTROSCOPY [J].

ANDO, T ;

YAMAMOTO, K ;

ISHII, M ;

KAMO, M ;

SATO, Y .

JOURNAL OF THE CHEMICAL SOCIETY-FARADAY TRANSACTIONS, 1993, 89 (19) :3635-3640

[3]

[Anonymous], 2019, Superhard Materials Market, 2025

[4]

Deutsche Keramische Gesellschaft DKG, 2014, Zukunftspotentiale von Hochleistungskeramiken

[5]

Evans C., 1962, P 5 BIENN C CARB, V1, P147

[6]

Гордеев С.К, 2015, [Композиты и наноструктуры, Composites and Nanostructures, Kompozity i nanostruktury], V7, P61

[7]

Gordeev S.K., 1999, Method of Manufacturing a Diamond -Silicon Carbide -Silicon Composite and a Composite Produced by This Method, Patent No. [WO9912866, 9912866]

[8] Low-pressure fabrication of diamond-SiC-Si composites [J].

Gordeev, SK ;

Zhukov, SG ;

Danchukova, LV ;

Ekstrom, TC .

INORGANIC MATERIALS, 2001, 37 (06) :579-583

[9] Boron-doped diamond with improved oxidation resistance [J].

Herrmann, M. ;

Matthey, B. ;

Gestrich, T. .

[10]

Herrmann M., 2018, Ceramic Applications, V1, P64

← 1 2 3 4 →