Nucleation activity of polyaniline coated short glass fiber towards isotactic polypropylene

被引：9
作者：
Cruz-Silva, R
Romero-García, J
Angulo-Sánchez, JL
机构：
[1] Ctr Invest Quim Aplicada, Saltillo 25100, Coahuila, Mexico
[2] UAEM, Ctr Invest Ingn & Ciencias Aplicadas, Cuernavaca 62210, Morelos, Mexico
来源：
JOURNAL OF MATERIALS SCIENCE | 2005年 / 40卷 / 18期
关键词：
D O I：
10.1007/s10853-005-1687-3
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of the polyaniline (PAn)-coated short glass fiber (SGF) on the crystallization behavior of isotactic polypropylene (iPP) was analyzed. The PAn-coated SGF was treated with an alkaline solution for 48 hr and throughly washed to remove the chlorine doping agent. The resulting dark blue fiber was redoped using a 4.0% wt p-toluensulfonic acid solution which, unlike chlorine, is a thermally stable doping agent for PAn up to 200 °C. Transcrystalline layers of the α-type crystal of polypropylene were formed around the fiber during non-isothermal crystallization.
引用
收藏
页码：5107 / 5109
页数：3
相关论文
共 20 条
[1]  
Arroyo N, 1997, POLYMER, V38, P5587, DOI 10.1016/S0032-3861(97)00102-X
[2]   Lamellar orientation in transcrystalline γ isotactic polypropylene nucleated on aramid fibers [J].
Assouline, E ;
Wachtel, E ;
Grigull, S ;
Lustiger, A ;
Wagner, HD ;
Marom, G .
MACROMOLECULES, 2002, 35 (02) :403-409
[3]   Nucleation activity of glass fibers towards iPP evaluated by DSC and polarizing light microscopy [J].
Bogoeva-Gaceva, G ;
Janevski, A ;
Mader, E .
POLYMER, 2001, 42 (09) :4409-4416
[4]  
Brandup J., 1988, POLYM HDB, V3
[5]  
CHANDRADAS N, 2005, POLYM INT, V54, P256
[6]   THE EFFECTS OF TRANSCRYSTALLINE INTERPHASE IN ADVANCED POLYMER COMPOSITES [J].
CHEN, EJH ;
HSIAO, BS .
POLYMER ENGINEERING AND SCIENCE, 1992, 32 (04) :280-286
[7]   Crystallization of the α and γ forms of isotactic polypropylene as a tool to test the degree of segregation of defects in the polymer chains [J].
De Rosa, C ;
Auriemma, F ;
Circelli, T ;
Waymouth, RM .
MACROMOLECULES, 2002, 35 (09) :3622-3629
[8]   DETERMINATION OF INTERFACIAL SHEAR-STRENGTH IN FIBER-REINFORCED THERMOPLASTIC COMPOSITES [J].
FOLKES, MJ ;
WONG, WK .
POLYMER, 1987, 28 (08) :1309-1314
[9]   Polymer matrix composites: Conductivity enhancement through polypyrrole coating of nickel flake [J].
Genetti, WB ;
Yuan, WL ;
Grady, BP ;
O'Rear, EA ;
Lai, CL ;
Glatzhofer, DT .
JOURNAL OF MATERIALS SCIENCE, 1998, 33 (12) :3085-3093
[10]   Dynamic mechanical and thermal properties of modified poly(propylene) wood fiber composites [J].
Hristov, V ;
Vasileva, S .
MACROMOLECULAR MATERIALS AND ENGINEERING, 2003, 288 (10) :798-806
12