Glass-Ceramics Obtained by the Crystallization of Basalt

被引：17

作者：

Cocic, M. ^{[1
]}

Logar, M. ^{[2
]}

Matovic, B. ^{[3
]}

Poharc-Logar, V. ^{[2
]}

机构：

[1] Univ Belgrade, Tech Fac Bor, Bor 19210, Serbia

[2] Univ Belgrade, Min & Geol Fac, Belgrade 11000, Serbia

[3] Vinca Inst, Belgrade 11000, Serbia

来源：

SCIENCE OF SINTERING | 2010年 / 42卷 / 03期

关键词：

Basalt; Glass-ceramics; phase composition; microstructure; mechanical properties; VITRIFICATION; INDUSTRIAL; WASTES;

D O I：

10.2298/SOS1003383C

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The possibility to obtain glass-ceramics from basalt from the locality on Vrelo (Kopaonik mt.) is shown in this paper. The parent rock was ground to fraction -0.4 +0.1 mm, and then melted at 1250 - 1300 degrees C. The crystallization melted bazaltic glass at 950 degrees C during the time interval of 3 hours caused synthesis of a glass-ceramic material with a microstructure that has excellent mechanical properties according to the determined dynamic modulus of elasticity and uniaxial compresive strength. The phase composition of. the obtained glass ceramic material was determined by XRPD using Rietveld refinement and SEM. Two phases were found: pyroxene which corresponds to omphacite of the composition (Na-0.199 K-0.180 Ca-0.471 Mg-0.249)(1.1)(Mg0.271Fe0.299Al0.430)(1.0)(Si1.704Ti0.046Al0.250)(2.0)O-6 and glass with on approximate relationship 69:31.

引用

页码：383 / 388

页数：6

共 30 条

[1] Effect of alumina on ceramic properties of cordierite glass-ceramic from basalt rock [J].