An analysis of hot deformation of an Al-Cu-Mg alloy produced by powder metallurgy

The high-temperature plasticity of a 2014 aluminium alloy produced by powder metallurgy was investigated in a wide range of temperatures and strain rates. When the strain rate was plotted as a function of stress (either peak flow stress in torsion, or applied stress in tensile creep), the alloy exhibited the same threshold-like behaviour observed in similar materials. The microstructure of representative torsioned samples was analysed in a transmission electron microscope (TEM) and the characteristics of particles and precipitate distribution were estimated. The dependence on stress and temperature was analysed by means of the conventional constitutive equations used for describing the hot-working behaviour and by means of a modified form of the sinh-equation, where the stress was substituted by an effective stress i.e. by the difference between the actual stress and a threshold stress. This temperature-dependent threshold stress was found to be a constant fraction (15%) of the Orowan stress generated by the dispersion of alumina particles and of precipitated intermetallic phases. (C) 2003 Elsevier Science B.V. All rights reserved.