Preparation of MoSi2-Al2O3 nano-composite via MASHS route

被引:21
作者
Ramezanalizadeh, Hossein [1 ]
Heshmati-Manesh, Saeed [1 ]
机构
[1] Univ Tehran, Sch Met & Mat Engn, Tehran 14395553, Iran
关键词
Molybdenum disilicide; MoSi2-Al2O3; nano-composite; MASHS; PCA; MOLYBDENUM DISILICIDE COMPOSITES; HIGH-TEMPERATURE SILICIDES; MOSI2; FABRICATION; POWDER; CREEP;
D O I
10.1016/j.ijrmhm.2011.11.005
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this study, MoSi2-Al2O3 nano-composite powder was prepared by mechanical alloying. Mixture of MoO3, Si and Al powders was exposed to high energy ball milling. Phase compositions and structural evolutions during milling were investigated by X-ray diffraction (XRD) analysis. The morphology of the milled powders was evaluated by scanning electron microscope (SEM). Within short milling times [15, 25 and 60 minutes in ball to powder weight ratios (BPR) of 35:1, 20:1 and 10:1, respectively], a combustion process occurred within the milling powder and the process mechanism was characterized to be mechanically activated self-propagating high-temperature synthesis (MASHS) type. From XRD results it was found that during the combustion process, MoO3 was completely reduced with Al and the resulting Mo reacted with Si to produce molybdenum disilicide and eventually a MoSi2-Al2O3 nano-composite powder formed within a short period of time. Further milling resulted in reduced mean crystallite sizes and increased lattice micro strain in the product phases. After 30 hours of milling in BPR of 35:1, the mean crystallite sizes were found to be 10, 9 and 11 nm for Al2O3, alpha-MoSi2 and beta-MoSi2, respectively. Also, effect of stearic acid addition as a Process Control Agent (PCA) was studied and the results showed that its usage postpones the reaction initiation and reduces mean crystallite sizes. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码:210 / 217
页数:8
相关论文
共 27 条
[1]   FABRICATION, STRUCTURE AND PROPERTIES OF MOSI2-BASE COMPOSITES [J].
ALMAN, DE ;
SHAW, KG ;
STOLOFF, NS ;
RAJAN, K .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1992, 155 (1-2) :85-93
[2]   SEQUENCE OF PHASE-FORMATION DURING MECHANICAL ALLOYING IN THE MO-SI SYSTEM [J].
BOKHONOV, BB ;
KONSTANCHUK, IG ;
BOLDYREV, VV .
JOURNAL OF ALLOYS AND COMPOUNDS, 1995, 218 (02) :190-196
[3]  
Cullity B.D., 1977, ELEMENTS XRAY DIFFRA, V2nd
[4]  
DAVID R, 2003, INTRO THERMODYNAMICS
[5]   REACTION SYNTHESIS OF HIGH-TEMPERATURE SILICIDES [J].
DEEVI, SC ;
THADHANI, NN .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 192 :604-611
[6]   IN-SITU SYNTHESIS OF MOSI2-AL2O3 COMPOSITE BY A THERMITE REACTION [J].
DEEVI, SC ;
DEEVI, S .
SCRIPTA METALLURGICA ET MATERIALIA, 1995, 33 (03) :415-420
[7]   Processing of MoSi2-based intermetallics [J].
Jayashankar, JS ;
Ross, EN ;
Eason, PD ;
Kaufman, MJ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 240 :485-492
[8]   PROCESSING OF MOLYBDENUM DISILICIDE [J].
JENG, YL ;
LAVERNIA, EJ .
JOURNAL OF MATERIALS SCIENCE, 1994, 29 (10) :2557-2571
[9]   Processing, microstructure and properties of C40Mo(Si,AI)2/Al2O3 composites [J].
Krakhmalev, PV ;
Ström, E ;
Sundberg, M ;
Li, C .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 360 (1-2) :207-213
[10]  
Lee CH, 2008, J CERAM PROCESS RES, V9, P321