Room-temperature synthesis and characterization of porous CeO2 thin films

被引：20

作者：

Chu, Dewei ^{[1
]}

Masuda, Yoshitake ^{[1
]}

Ohji, Tatsuki ^{[1
]}

Kato, Kazumi ^{[1
]}

机构：

[1] Natl Inst Adv Ind Sci & Technol, Moriyama Ku, Nagoya, Aichi 4638560, Japan

来源：

PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE | 2012年 / 209卷 / 01期

关键词：

CeO2 thin films; electrodeposition; photoluminescence; SITE-SELECTIVE DEPOSITION; CERIUM OXIDE; CONTROLLED GROWTH; NANOSTRUCTURES; ELECTRODEPOSITION; OXIDATION; ARRAYS;

D O I：

10.1002/pssa.201127291

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

CeO2 thin films with hexagonal-shaped pores were successfully prepared by a facile electrodeposition at room temperature combined with an etching process. By using electrodeposited ZnO nanorods as a soft template, the morphology, and microstructure of the CeO2 could be controlled. TEM observation indicated that as-prepared CeO2 film is composed of nanocrystals with average size of several nanometers, while XPS analysis showed the coexistence of Ce3+ and Ce4+ in the film. The photoluminescence properties of CeO2 films were measured, which showed much higher sensitivity compared to bare substrate. (C) 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

引用

页码：139 / 142

页数：4

共 22 条

[21] Hydrothermal preparation of fractal dendrites: Cerium carbonate hydroxide and cerium oxide [J].

Wu, Mingzai ;

Zhang, Qihua ;

Liu, Yanmei ;

Fang, Qingqing ;

Liu, Xiansong .

MATERIALS RESEARCH BULLETIN, 2009, 44 (06) :1437-1440

[22] Preparation of Core/Shell and Hollow Nanostructures of Cerium Oxide by Electrodeposition on a Polystyrene Sphere Template [J].

Yamaguchi, Ippei ;

Watanabe, Mitsuru ;

Shinagawa, Tsutomu ;

Chigane, Masaya ;

Inaba, Minoru ;

Tasaka, Akimasa ;

Izaki, Masanobu .

ACS APPLIED MATERIALS & INTERFACES, 2009, 1 (05) :1070-1075

← 1 2 3 →