Properties of concrete incorporating fine recycled aggregate

被引:600
作者
Khatib, JM [1 ]
机构
[1] Sheffield Hallam Univ, MERI, Ctr Infrastructure Management, Sheffield S1 1WB, S Yorkshire, England
关键词
expansion; fine recycled aggregate; mechanical properties; nondestructive testing; shrinkage;
D O I
10.1016/j.cemconres.2004.06.017
中图分类号
TU [建筑科学];
学科分类号
0813 ;
摘要
The properties of concrete containing fine recycled aggregate are investigated. Recycled aggregate consisted of crushed concrete (CC) or crushed brick (CB) with particles less than 5 mm in diameter. The free water/cement ratio was kept constant for all mixes. The fine aggregate in concrete was replaced with 0%, 25%, 50% and 100% CC or CB. Generally, there is strength reduction of 15-30% for concrete containing CC. However, concrete incorporating up to 50% CB exhibits similar long-term strength to that of the control. Even at 100% replacement of fine aggregate with CB, the reduction in strength is only 10%. Beyond 28 days of curing, the rate of strength development in concrete containing either CC or CB is higher than that of the control indicating further cementing action in the presence of fine recycled aggregate. More shrinkage and expansion occur in concrete containing CC or CB. (c) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码:763 / 769
页数:7
相关论文
共 14 条
[1]  
*ACI COMM 209, 1992, PRED CREEP SHRINK TE, P47
[2]  
[Anonymous], 1994, MATER STRUCT, V27, P557, DOI DOI 10.1007/BF02473217
[3]  
Banthia N, 2000, Concr Int, V22, P41
[4]  
Barragán RM, 2001, ING HIDRAUL MEX, V16, P113
[5]   Use of building rubbles as recycled aggregates [J].
Chen, HJ ;
Yen, T ;
Chen, KH .
CEMENT AND CONCRETE RESEARCH, 2003, 33 (01) :125-132
[6]   Suitability of recycled concrete aggregate for use in BS 5328 designated mixes [J].
Dhir, RK ;
Limbachiya, MC ;
Leelawat, T .
PROCEEDINGS OF THE INSTITUTION OF CIVIL ENGINEERS-STRUCTURES AND BUILDINGS, 1999, 134 (03) :257-274
[7]  
Huo XMS, 2001, ACI MATER J, V98, P440
[8]   Properties of concrete made with recycled aggregate from partially hydrated old concrete [J].
Katz, A .
CEMENT AND CONCRETE RESEARCH, 2003, 33 (05) :703-711
[9]   SOME FACTORS AFFECTING THE DYNAMIC MODULUS OF ELASTICITY OF HIGH-STRENGTH CONCRETE [J].
LYDON, FD ;
IACOVOU, M .
CEMENT AND CONCRETE RESEARCH, 1995, 25 (06) :1246-1256
[10]   Relative moisture movement through recycled aggregate concrete [J].
Padmini, AK ;
Ramamurthy, K ;
Mathews, MS .
MAGAZINE OF CONCRETE RESEARCH, 2002, 54 (05) :377-384