Experimental study of the material and bond properties of frost-damaged concrete

被引：153

作者：

Hanjari, Kamyab Zandi ^{[1
]}

Utgenannt, Peter ^{[2
]}

Lundgren, Karin ^{[1
]}

机构：

[1] Chalmers Univ Technol, Dept Civil & Environm Engn, S-41296 Gothenburg, Sweden

[2] CBI Swedish Cement & Concrete Res Inst, S-50115 Boras, Sweden

来源：

CEMENT AND CONCRETE RESEARCH | 2011年 / 41卷 / 03期

关键词：

Freezing and thawing; Compressive strength; Tensile properties; Bond strength; Fracture energy; INTERNAL DAMAGE; STRENGTH; RESISTANCE; CYCLES;

D O I：

10.1016/j.cemconres.2010.11.007

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In an extensive experimental investigation, several types of tests were conducted on a reference specimen and frost-damaged concrete. Two levels of internal frost damage were quantified by the relative dynamic modulus of elasticity and compressive strength. Test results showed a significant influence of freeze-thaw cycles on the compressive strength and even more influence on the modulus of elasticity and the compressive strain at peak stress. Reduced tensile strength and increased fracture energy were measured. From inverse analysis of wedge splitting test results, a significant effect of frost on the shape of the tensile stress-crack opening relationship was observed: tensile strength was reduced, while the post-peak behaviour was more ductile for the frost-damaged concrete. Pull-out tests showed the influence of freeze-thaw cycles on bond strength and slip. The pull-out test results are compared with similar tests available in the literature and the effect of frost on bond behaviour is discussed. (C) 2010 Elsevier Ltd. All rights reserved.

引用

页码：244 / 254

页数：11

共 26 条

[1]

Beaudoin JJ., 1974, Cem Concr Res, V4, P139, DOI DOI 10.1016/0008-8846(74)90128-8

[2]

Cornelissen H, 1986, Heron, V31, P45

[3] Determining the tensile stress-crack opening curve of concrete by inverse analysis [J].

de Oliveira, JLA ;

Gettu, R .

JOURNAL OF ENGINEERING MECHANICS, 2006, 132 (02) :141-148

[4]

Fagerlund G., 1994, EFFECT FROST DAMAGE

[5]

Fagerlund G., 2004, SERVICE LIFE MODEL I, DOI [10.1007/s13398-014-0173-7.2, DOI 10.1007/S13398-014-0173-7.2]

[6]

Fagerlund G., 2001, MANUAL ASSESSING CON

[7]

Gong Jin-xin, 2005, Journal of Dalian University of Technology, V45, P405

[8]

HANJARI KZ, 2008, 200810 CHALMERS U TE

[9]

HANJARI KZ, 2008, THESIS CHALMERS U TE

[10]

HASAN M., 2004, J ADV CONCR TECHNOL, V2, P89, DOI DOI 10.3151/JACT.2.89

← 1 2 3 →