The evolution of η phase in Ni-Co base superalloys

被引：57

作者：

Cui, C. Y. ^{[1
]}

Gu, Y. F. ^{[1
]}

Ping, D. H. ^{[1
]}

Harada, H. ^{[1
]}

Fukuda, T. ^{[1
]}

机构：

[1] Natl Inst Mat Sci, High Temp Mat Ctr, Tsukuba, Ibaraki 3050047, Japan

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 485卷 / 1-2期

关键词：

Ni-Co base superalloys; heat treatment; eta phase;

D O I：

10.1016/j.msea.2007.08.047

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The evolution of a eta phase (Ni(3)Ti) in Ni-Co base superalloys with different Co and Ti content has been investigated. The results showed that the eta phase existed in the samples with 23.1 wt.%Co and 5.4 wt.%Ti (TMW-3) and also the samples with 28.6 wt.% Co and 7.4 wt.%Ti (TMW-5) heat-treated at the temperature ranges of 1100-1140 degrees C, but not in the samples with 26.3 wt.%Co and 6.0 wt.%Ti (TMW-4). Even in TMW-3 and TMW-5, higher solution temperature (1180 degrees C) can fully reduce the formation of the eta phase. The evolution of the eta phase is complicated and may be related to the Ti content, Ti/Al ratio and alloy's composition. (C) 2007 Elsevier B.V. All rights reserved.

引用

页码：651 / 656

页数：6

共 16 条

[1]

*ASTM, 2005, E56202 ASTM

[2]

Bouse GK, 1996, SUPERALLOYS 1996, P163

[3] MICROSTRUCTURE AND HYDROGEN EFFECTS ON FRACTURE IN THE ALLOY-A-286 [J].

BROOKS, JA ;

THOMPSON, AW .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1993, 24 (09) :1983-1991

[4] Phase stability and yield stress of Ni-base superalloys containing high Co and Ti [J].

Cui, C. Y. ;

Gu, Y. F. ;

Harada, H. ;

Ping, D. H. ;

Sato, A. .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (11) :3183-3190

[5]

Cui CY, 2005, METALL MATER TRANS A, V36A, P2921

[6]

CUI CY, 2007, TMS 2007 ANN M EXH F, P107

[7] γ′ formation in superalloy U720LI [J].

Furrer, DU ;

Fecht, HJ .

SCRIPTA MATERIALIA, 1999, 40 (11) :1215-1220

[8]

GABB TP, NASATM2004213066

[9] New Ni-Co-base disk superalloys with higher strength and creep resistance [J].

Gu, Y. ;

Harada, H. ;

Cui, C. ;

Ping, D. ;

Sato, A. ;

Fujioka, J. .

SCRIPTA MATERIALIA, 2006, 55 (09) :815-818

[10] Heat treatment of UDIMET 720Li: the effect of microstructure on properties [J].

Jackson, MP ;

Reed, RC .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 259 (01) :85-97

← 1 2 →