Comparison of the fracture and fatigue properties of 16MnR steel weld metal, the HAZ and the base metal

被引：0
作者：
Gao, ZL
Zhang, KD
机构：
来源：
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 1997年 / 63卷 / 1-3期
关键词：
fracture; fatigue; weld metal; base metal; HAZ;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The fracture toughness and fatigue crack growth rate of 16MnR steel weld metal, the HAZ and the base metal were measured. The fracture toughness J(1c) of the HAZ is lowest among the weld and base metals and the HAZ, the J(1c) of the base metal being a little higher than that of the HAZ and that of the weld metal being the highest. The crack growth in the HAZ is faster than those in the weld and the base metal, which are nearly the same. Thus both the fracture and fatigue properties in the HAZ are worse than those in both the weld and the base metals.
引用
收藏
页码：559 / 562
页数：4
相关论文
共 50 条
[21]   Degradation of impact fracture during accelerated ageing of weld metal on microalloyed steel [J].
Vargas-Arista B. ;
Hallen J.M. ;
Albiter A. ;
Ángeles-Chávez C. .
Welding International, 2010, 24 (04) :315-320
[22]   THE EFFECT OF HEAT INPUT ON THE FRACTURE BEHAVIOUR OF SURFACE WELD METAL OF RAIL STEEL [J].
Popovic, Olivera ;
Prokic-Cvetkovic, Radica ;
Radovic, Ljubica ;
Burzic, Zijah ;
Arsic, Dusan .
STRUCTURAL INTEGRITY AND LIFE-INTEGRITET I VEK KONSTRUKCIJA, 2020, 20 (01) :77-81
[23]   Tensile properties and microstructure of weld metal of X80 steel [J].
Motohashi, H ;
Hagiwara, N ;
Masuda, T .
THERMEC'2003, PTS 1-5, 2003, 426-4 :4013-4018
[24]   Fracture Toughness of Weld Metal of 440 MPa Grade High-strength Steel [J].
Zeng D. ;
An T. ;
Zheng S. ;
Dai H. ;
Cao Z. ;
Ma C. .
Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2024, 38 (02) :151-160
[25]   Sigma phase precipitation and its influence on hydrogen induced cracking of duplex stainless steel base metal and weld metal [J].
K. Nakade .
Welding in the World, 2003, 47 (9-10) :9-20
[26]   On locations initiating cleavage fracture in precracked specimens of low alloy steel and weld metal [J].
G.Z. Wang ;
J.H. Chen .
International Journal of Fracture, 2001, 108 :235-250
[27]   On locations initiating cleavage fracture in precracked specimens of low alloy steel and weld metal [J].
Wang, GZ ;
Chen, JH .
INTERNATIONAL JOURNAL OF FRACTURE, 2001, 108 (03) :235-250
[28]   Corrosion and fatigue characteristics of positively polarised Zeron 100 base & weld metal in synthetic seawater [J].
Comer, A ;
Looney, L .
INTERNATIONAL JOURNAL OF FATIGUE, 2006, 28 (08) :826-834
[29]   Microstructure and Mechanical Properties of GMAW Weld Metal of 890 MPa Class Steel [J].
Yun Peng ;
Xing-na Peng ;
Xiao-mu Zhang ;
Zhi-ling Tian ;
Tao Wang .
Journal of Iron and Steel Research International, 2014, 21 :539-544
[30]   Improvement of mechanical properties of ferritic stainless steel weld metal by ultrasonic vibration [J].
Watanabe, Takehiko ;
Shiroki, Masataka ;
Yanagisawa, Atsushi ;
Sasaki, Tomohiro .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2010, 210 (12) :1646-1651
12345