Bright dual-mode green emission and temperature sensing properties in Er3+/Yb3+ co-doped MgWO4 phosphor

Er3+/Yb3+ co-doped MgWO4 phosphor was synthesized by a solid state reaction method and the phase, photoluminescence and temperature sensing properties were analyzed. The phosphor has shown intense visible green emission via up-conversion process on near-infrared (980 nm) excitation and down-conversion process on 379 nm excitation and thus behaves as a dual-mode phosphor. In the up-conversion and down-conversion emission, the H-2(11/2) -> I-4(15/2) and S-4(3/2) -> I-4(15/2) transitions of the Er3+ ion portray a temperature dependent behavior and have been used for optical temperature sensor by means of the fluorescence intensity ratio method. Moreover, we compared the curves of S in the continuous temperature range (83-583 K) and the two sectional temperature ranges in up-conversion process. It is found that the phosphor can be operated over a temperature range of 83-583 K with a maximum sensitivity of about 0.0093 K-1 at 583 K. The results indicate that the Er3+/Yb3+ co-doped MgWO4 phosphor is a potential candidate to be used in display devices and optical temperature sensors.