Make nanostructured metal exceptionally tough by introducing non-localized fracture behaviors

被引：69

作者：

Chen, Ai-Ying ^{[1
,2
]}

Li, Dong-Feng ^{[1
]}

Zhang, Jun-Bao ^{[3
]}

Song, Hong-Wei ^{[3
]}

Lu, Jian ^{[1
]}

机构：

[1] Hong Kong Polytech Univ, Dept Mech Engn, Hong Kong, Hong Kong, Peoples R China

[2] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Shanghai 200030, Peoples R China

[3] Baosteel Technol Ctr, Shanghai 201900, Peoples R China

来源：

SCRIPTA MATERIALIA | 2008年 / 59卷 / 06期

关键词：

nanostructured materials; yield strength; ductility;

D O I：

10.1016/j.scriptamat.2008.04.048

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A new method for manufacturing nanomaterials with high ductility on a large scale is reported here. Based on surface nanocrystallization and warm co-rolling technologies, the resulting material amazingly exhibits high strength and exceptional ductility. Stainless steel was selected to demonstrate the extensibility of our approach. The yield strength (878 MPa) is more than double that of the monolithic material. The elongation to failure (48%) triples comparing with the material with the same yield strength obtained by work hardening. (C) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

引用

页码：579 / 582

页数：4

共 25 条

[1] Fracture toughness and R-curve behavior of laminated brittle-matrix composites [J].

Bloyer, DR ;

Rao, KTV ;

Ritchie, RO .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (10) :2483-2496

[2] Tensile properties of a nanocrystalline 316L austenitic stainless steel [J].

Chen, XH ;

Lu, J ;

Lu, L ;

Lu, K .

SCRIPTA MATERIALIA, 2005, 52 (10) :1039-1044

[3] A SIMPLE WAY TO MAKE TOUGH CERAMICS [J].

CLEGG, WJ ;

KENDALL, K ;

ALFORD, NM ;

BUTTON, TW ;

BIRCHALL, JD .

NATURE, 1990, 347 (6292) :455-457

[4] PERSPECTIVE ON THE DEVELOPMENT OF HIGH-TOUGHNESS CERAMICS [J].

EVANS, AG .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (02) :187-206

[5] Crack arrest and multiple cracking in class through the use of designed residual stress profiles [J].

Green, DJ ;

Tandon, R ;

Sglavo, VM .

SCIENCE, 1999, 283 (5406) :1295-1297

[6]

HARVEY PD, 1999, ENG PROPERTIES STEEL, P275

[7] Hardening by annealing and softening by deformation in nanostructured metals [J].

Huang, XX ;

Hansen, N ;

Tsuji, N .

SCIENCE, 2006, 312 (5771) :249-251

[8] Optimization of strength and ductility in nanocrystalline and ultrafine grained metals [J].

Koch, CC .

SCRIPTA MATERIALIA, 2003, 49 (07) :657-662

[9] Mechanical behavior of nanocrystalline metals and alloys [J].

Kumar, KS ;

Van Swygenhoven, H ;

Suresh, S .

ACTA MATERIALIA, 2003, 51 (19) :5743-5774

[10]

Lu K, 1999, J MATER SCI TECHNOL, V15, P193

← 1 2 3 →