Spectral properties of Tm,Ho:LiYF4 laser crystal

The LiYF4 single crystal codoped with thulium and holmium ions was successfully grown by the Cz method. The optimal technical parameters obtained were as follows: the pulling rate was 0.16 mm/h; the rotation speed was 3 rpm; the cooling rate was 15 degrees C/h. The result of XRD curve showed that as-grown Tm,Ho:LiYF4 laser crystal belonged to the monoclinic system with scheelite-type structure and space group I41/a. The cell parameters calculated were: a=0.52160 nm, c=1.09841 nm and Z=4. Absorption and fluorescence spectra of Tm,Ho:LiYF4 laser crystal at room temperature were measured and analysed. The absorption cross section, FWHM and absorption coefficient at 779.3 nm calculated were 7.44x10(-21) cm(2), 8.7 nm and 2.23 cm(-1), respectively. An intensive fluorescence emission peak appeared near 2045 nm. The emission cross section and fluorescence lifetime were 0.87x10(-20) cm(2) and 10.8 ms, respectively. The ratio of Tm-Ho transfer to its back-transfer process was 10.6.