Stress assisted oxide cracking of Zr-2.5Nb pressure tube material

被引：0
|
作者：
Gopalan, Avinash [1 ]
Sunil, Saurav [1 ]
Murty, T. N. [1 ]
Bind, A. K. [1 ]
Kumawat, B. K. [1 ]
Chandanshive, S. A. [1 ]
Singh, R. N. [1 ]
机构：
[1] Bhabha Atom Res Ctr BARC, Mech Met Div MMD, Mumbai 400085, Maharashtra, India
来源：
JOURNAL OF NUCLEAR MATERIALS | 2020年 / 536卷 / 536期
关键词：
DELAYED HYDRIDE CRACKING; DYNAMIC EMBRITTLEMENT; FRACTURE-TOUGHNESS; ALLOY; OXIDATION; ZIRCONIUM; GROWTH; NB; BEHAVIOR; TIP;
D O I：
10.1016/j.jnucmat.2020.152187
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The crack growth rates of un-irradiated and un-hydrided Zr-2.5Nb pressure tube material has been investigated in both air and in vacuum. Pre-cracked CCT samples made from pressure tube were tested in air atmosphere at 300 °C and 350 °C at different stress intensity factors. It was observed that till a particular stress intensity factor there is no crack growth and after which the crack growth rate increases with increase in stress intensity factor. For the test carried out in vacuum, it was observed that the crack growth rates for air is an order of magnitude higher than that of the crack growth obtained in the vacuum ambience. © 2020 Elsevier B.V.
引用
收藏
页数：9
相关论文
共 50 条
  • [41] Overload fracture of hydrided region at simulated blunt flaws in Zr-2.5Nb pressure tube material
    Cui, Jun
    Shek, Gordon K.
    Proceedings of the ASME Pressure Vessels and Piping Conference 2005, Vol 6, 2005, 6 : 129 - 143
  • [42] Load separability and ηpl factor determination for CT specimen of Zr-2.5Nb pressure tube material
    Bind, A. K.
    Singh, R. N.
    ENGINEERING FRACTURE MECHANICS, 2020, 224
  • [43] Crack growth resistance of irradiated Zr-2.5Nb pressure tube material at low hydrogen levels
    Davies, PH
    Himbeault, DD
    Shewfelt, RSW
    Hosbons, RR
    EFFECTS OF RADIATION ON MATERIALS: 20TH INTERNATIONAL SYMPOSIUM, 2001, 1045 : 846 - 868
  • [44] Role of microchemistry and microstructure on variability in corrosion and deuterium uptake of Zr-2.5Nb pressure tube material
    Warr, BD
    Perovic, V
    Lin, YP
    Wallace, AC
    ZIRCONIUM IN THE NUCLEAR INDUSTRY: THIRTEENTH INTERNATIONAL SYMPOSIUM, 2002, 1423 : 313 - 336
  • [45] Effects of Hydride Morphology and Test Temperature on Fracture Toughness of Zr-2.5Nb Pressure Tube Material
    Cui, Jun
    Shek, Gordon K.
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, VOL 6, PTS A AND B, 2010, : 81 - 96
  • [46] Threshold stress intensity factor, KIH for delayed hydride cracking of a Zr-2.5Nb tube with loading mode
    Kim, Young Suk
    Park, Sun Sam
    Kwun, Sook In
    JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 462 (1-2) : 367 - 375
  • [47] Influence of loading rate and hydrogen content on fracture toughness of Zr-2.5Nb pressure tube material
    Bind, A. K.
    Singh, R. N.
    Khandelwal, H. K.
    Sunil, S.
    Avinash, G.
    Chakravartty, J. K.
    Stahle, P.
    JOURNAL OF NUCLEAR MATERIALS, 2015, 465 : 177 - 188
  • [48] Experimental observations of void growth in the Zr-2.5Nb pressure tube alloy
    Peace, R
    Miller, RE
    JOURNAL OF NUCLEAR MATERIALS, 2005, 341 (2-3) : 231 - 234
  • [49] Anisotropy and variability in thermal creep behaviour of Zr-2.5Nb pressure tube
    Patel, Vivek
    Gopalan, Avinash
    Khandelwal, Harshit K.
    Keskar, Nachiket
    Devi, Y. Pushpalatha
    Singh, R. N.
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2022, 200
  • [50] Evaluation of a delayed hydride cracking in Zr-2.5Nb CANDU and RBMK pressure tubes
    Gou, Yuan
    Li, Yanrong
    Liu, Yanzhang
    Chen, Hongtong
    Ying, Shihao
    MATERIALS & DESIGN, 2009, 30 (04) : 1231 - 1235
12345