Preparation and characterization of porous Al2O3 based on nano-Al2O3 powders and PLA template by microwave sintering

被引：0
|
作者：
He, Zhenhua [1 ]
Zhu, Shifei [1 ]
Liu, Canhui [1 ]
机构：
[1] Wuhan Univ Technol, Sch Informat Engn, Wuhan 430070, Peoples R China
来源：
PROCESSING AND APPLICATION OF CERAMICS | 2020年 / 14卷 / 02期
基金：
中国国家自然科学基金;
关键词：
porous Al2O3; 3D printing; microwave sintering; advanced manufacturing; ALUMINA; CERAMICS; FABRICATION;
D O I：
10.2298/PAC2002128H
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Macroporous and mesoporous Al2O3 body was prepared using mesh screening shaped polylactic acid (PLA) template. The mesh screening shaped PLA template was made from 3D cylindrical model by adjusting the PLA filling rate at 30 vol. %. After 3D printing, the PLA template was filled with Al2O3 nano powders and microwave sintered at 1673 K for 20 min. During the sintering, the PLA template was decomposed and left large pores which could promote sintering of Al2O3. The Al2O3 sintered body showed macroporous structure with the pore size of 100 to 300 nm and also mesoporosity with local single crystal structure. The average pore diameter of mesoporous structures in the Al2O3 sintered body was about 7.6 nm. The Vickers hardness of the porous Al2O3 is 1.254 +/- 0.039 GPa. The obtained results confirmed that 3D-printed PLA template assisted microwave sintering is a promising technical processing for the fabrication of macroporous and mesoporous Al2O3 with local single crystal structure.
引用
收藏
页码：128 / 133
页数：6
相关论文
共 50 条
  • [1] Preparation and Characterization of the Charged Nano-Al2O3
    Wang, Qiangsheng
    Li, Jianfen
    Ren, Shidong
    Fan, Guozhi
    Wang, Mei
    2015 2ND INTERNATIONAL CONFERENCE ON MATERIAL ENGINEERING AND APPLICATION (ICMEA 2015), 2015, : 589 - 594
  • [2] MICROWAVE SINTERING OF AL2O3
    VODEGEL, S
    HANNAPPEL, C
    WILLERTPORADA, M
    METALL, 1994, 48 (03): : 206 - 210
  • [3] Sintering of α-Al2O3-seeded nanocrystalline γ-Al2O3 powders
    Nordahl, CS
    Messing, GL
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (04) : 415 - 422
  • [4] Preparation of nano Ni/Al2O3 composite powders
    Yan, QF
    Huang, ZR
    Dong, SM
    Jiang, DL
    HIGH-PERFORMANCE CERAMICS III, PTS 1 AND 2, 2005, 280-283 : 1107 - 1110
  • [5] Effect of nano-Al2O3 particles on the NiP/nano-Al2O3 coatings' properties
    Yuan, Xuetao
    Hua, Zhiqiang
    Wang, Lei
    Sun, Dongbai
    Chen, Songlin
    MECHANICAL, MATERIALS AND MANUFACTURING ENGINEERING, PTS 1-3, 2011, 66-68 : 1668 - +
  • [6] Microwave assisted sintering of Al2O3
    Leparoux, S
    Walter, G
    Lampke, T
    Wielage, B
    ADVANCES IN MICROWAVE AND RADIO FREQUENCY PROCESSING, 2006, : 583 - +
  • [7] Influence of characteristics of Al2O3 powders on the sintering performance of β double prime -Al2O3
    Chen, Kungang
    Lin, Zuxiang
    Xu, Xiaohe
    Li, Xiangting
    Wuji Cailiao Xuebao/Journal of Inorganic Materials, 1997, 12 (03): : 327 - 330
  • [8] Preparation and characterization of Al2O3 coated graphite powders
    Wang, ZF
    Wang, HZ
    Hong, YR
    Deng, CG
    HIGH-PERFORMANCE CERAMICS III, PTS 1 AND 2, 2005, 280-283 : 1671 - 1674
  • [9] Preparation and characterization of nano-sized Al2O3/ZrO2 powders
    Chen, Guo-Qing
    Zhang, Kai-Feng
    Wang, Guo-Feng
    Zhang, Lei
    Cailiao Kexue yu Gongyi/Material Science and Technology, 2004, 12 (01): : 20 - 23
  • [10] Fabrication of porous Al2O3 by microwave sintering and its properties
    Oh, ST
    Tajima, K
    Ando, M
    Ohji, T
    MATERIALS LETTERS, 2001, 48 (3-4) : 215 - 218
12345