The impact of thermal treatment conditions on the formation of crystalline structure of Ce-Zr-oxide composite obtained by a modified sol-gel technique

We present the results of the modified sol-gel synthesis of ultrafine ceria-doped zirconia powder for medical ceramics (implants) and catalytic purposes (environmental catalysis and petrochemistry). Special attention has been paid to study the influence of thermal treatment on crystallite size and crystal lattice parameters of zirconia doped by ceria. Zirconyl chloride and cerium nitrate were used as metal sources, and tetraethylammonium hydroxide (TEAH) was used as a sol stabilizer at molar ratio TEAH/Sigma (Ce + Zr) equal to 0.5. It was proved that zirconium and cerium practically completely were included in the obtained solid solutions, since their phase compositions fully correspond to initial quantities of cerium and zirconium in reaction mixture. It was shown that average crystallite size of the obtained powders did not exceed 75 angstrom, and the powders were resistant to thermal treatment. It was established that stabilization of the crystal lattice of ZrO2 occurs through formation of a cubic ceria sublattice.