Combustion synthesis process of Ag added Al3Ti intermetallic compound

被引:0
作者
Miyazaki, Y [1 ]
Uenishi, K [1 ]
Kobayashi, KF [1 ]
机构
[1] Osaka Univ, Dept Mfg Sci, Suita, Osaka 5650871, Japan
来源
DESIGNING, PROCESSING AND PROPERTIES OF ADVANCED ENGINEERING MATERIALS, PTS 1 AND 2 | 2004年 / 449-4卷
关键词
titanium aluminide(Al3Ti); intermetallic compound; powder metallurgy; combustion synthesis; hot press;
D O I
10.4028/www.scientific.net/MSF.449-452.201
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The effect of Ag addition to the mixture of Al and Ti on the densification of synthesized Al-Ti intermetallic compounds was examined. By the Ag addition, ignition temperature to form Al3Ti was lowered to the eutectic temperature of the Al-Ag alloy. When elemental powder mixture with 2% Ag was continuously heated to 973K under the uniaxial pressure of 1.0MPa, void ratio of sintered compact was reduced to 0.1% and the densification was enhanced by increasing the composition of Ag. Al3Ti and Ag2Al were formed in the as sintered compact and Ag2Al decomposed to solve Ag into Ll(2)-Al3Ti by further heating at 1073K for 14.4ks. Although Ag addition decreased the hardness of sintered compact lower than that of Al3Ti, it still retained the hardness of about 40OHv for 12% Ag added specimen. The sintered compact was hardly damaged after oxidizing at 1273K for 230.4ks due to the formation of protective Al2O3 surface scale.
引用
收藏
页码:201 / 204
页数:4
相关论文
共 7 条
[1]  
KOSTER W, 1957, Z METALLKD, V48, P331
[2]   DEFORMATION AND FRACTURE OF TIAL AT ELEVATED-TEMPERATURES [J].
LIPSITT, HA ;
SHECHTMAN, D ;
SCHAFRIK, RE .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (11) :1991-1996
[3]   Fabrication of a thick surface layer of Al3Ti on Ti substrate by reactive-pulsed electric current sintering [J].
Matsubara, T ;
Shibutani, T ;
Uenishi, K ;
Kobayashi, KF .
INTERMETALLICS, 2000, 8 (07) :815-822
[4]   Processing of intermetallic compounds for structural applications at high temperature [J].
Uenishi, K ;
Kobayashi, KF .
INTERMETALLICS, 1996, 4 :S95-S101
[5]  
UENISHI K, 1992, Z METALLKD, V83, P241
[6]   Formation of surface layer based on Al3Ti on aluminum by laser cladding and its compatibility with ceramics [J].
Uenishi, K ;
Kobayashi, KF .
INTERMETALLICS, 1999, 7 (05) :553-559
[7]  
Uenishi K, 1999, Z METALLKD, V90, P163