Twin wall distortions through structural investigation of epitaxial BiFeO3 thin films

In this work, epitaxial (001) BiFeO3 thin films were deposited on SrTiO3 and TbScO3 single-crystal substrates and analyzed with high-resolution x-ray diffraction-reciprocal space mapping. A basic method was developed to extract structural details of the as-grown BiFeO3 film, including (i) epitaxial strain, (ii) ferroelastic domains, and (iii) lattice rotations. After demonstrating the method, extrinsic distortions at vertical twin walls were determined for specific BiFeO3 heterostructures. A relatively large distortion (0.20 +/- 0.08) was measured in a multidomain (12) and incoherent film, while a nearly intrinsic distortion (0.04 +/- 0.03) was measured in a two-domain coherent film. This work offers insights into the structure of multiferroic BiFeO3 thin films with a general approach that is appropriate for low symmetry epitaxial heterostructures.