Solvothermal synthesis and magnetic properties of β-Co2P nanorods

被引：3
|
作者：
Li, Tian [1 ]
Liao, Jun Peng [2 ]
Wang, Ying Feng [3 ]
机构：
[1] Yue Yang Vocat Tech Coll, Yueyang 414000, Hunan, Peoples R China
[2] Yue Yang Coll Tradit Chinese Med, Yueyang 414000, Hunan, Peoples R China
[3] Capital Normal Univ, Dept Chem, Beijing 100048, Peoples R China
来源：
MATERIALS SCIENCE-POLAND | 2015年 / 33卷 / 02期
关键词：
solvothermal synthesis; magnetic materials; intermetallic alloys and compounds; nanocrystalline materials; TRANSITION-METAL PHOSPHIDES; ROUTE; FE2P; PRECURSORS; REDUCTION; PNICTIDES; NI2P;
D O I：
10.1515/msp-2015-0049
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Hexagonal high temperature phase beta-Co2P nanorods with a diameter of around 50 nm were synthesized via a mild solvothermal route. The reaction was carried out at 180 degrees C using cobalt chloride hexahydrate (CoCl2 center dot 6H(2)O) as Co source and yellow phosphorous as P source. The composition, structure as well as morphology were characterized by X-ray diffraction (XRD), X-ray photoemission spectroscopy (XPS) and transmission electron microscopy (TEM). The magnetic susceptibility curve indicates that the beta-Co2P nanorods show canted antiferromagnetic state, different from the paramagnetic state of orthorhombic low temperature phase beta-Co2P.
引用
收藏
页码：312 / 316
页数：5
相关论文
共 50 条
  • [21] Structural and magnetic properties of Co1-xZnxFe2O4 nanorods prepared by the solvothermal annealing method
    Jia, Zhigang
    Ren, Daping
    Wang, Qiuze
    Xu, Lixin
    Zhu, Rongsun
    CERAMICS INTERNATIONAL, 2013, 39 (06) : 6113 - 6118
  • [22] Solvothermal synthesis and magnetic properties of pyrite Co1-xFexS2 with various morphologies
    Han, JT
    Huang, YH
    Huang, W
    MATERIALS LETTERS, 2006, 60 (15) : 1805 - 1808
  • [23] Hollow Co2P nanoflowers assembled from nanorods for ultralong cycle-life supercapacitors
    Cheng, Ming
    Fan, Hongsheng
    Xu, Yingying
    Wang, Rongming
    Zhang, Xixiang
    NANOSCALE, 2017, 9 (37) : 14162 - 14171
  • [24] Co2P nanoparticles for microwave absorption
    Green, Michael
    Tian, Lihong
    Xiang, Peng
    Murowchick, James
    Tan, Xinyu
    Chen, Xiaobo
    MATERIALS TODAY NANO, 2018, 1 : 1 - 7
  • [25] Shape-Controlled Synthesis of Co2P Nanostructures and Their Application in Supercapacitors
    Chen, Xiaojuan
    Cheng, Ming
    Chen, Di
    Wang, Rongming
    ACS APPLIED MATERIALS & INTERFACES, 2016, 8 (06) : 3892 - 3900
  • [26] Favorable Core/Shell Interface within Co2P/Pt Nanorods for Oxygen Reduction Electrocatalysis
    Liu, Chang
    Ma, Zhong
    Cui, Meiyang
    Zhang, Zhiyong
    Zhang, Xu
    Su, Dong
    Murray, Christopher B.
    Wang, Jia X.
    Zhang, Sen
    NANO LETTERS, 2018, 18 (12) : 7870 - 7875
  • [27] DIE KRISTALLSTRUKTUR VON CO2P
    NOWOTNY, H
    ZEITSCHRIFT FUR ANORGANISCHE CHEMIE, 1947, 254 (1-2): : 31 - 36
  • [28] FORMATION OF CO2P IN THE COMBUSTION REGIME
    MUCHNIK, SV
    LYNCHAK, KA
    DUBROV, AN
    COMBUSTION EXPLOSION AND SHOCK WAVES, 1983, 19 (01) : 35 - 37
  • [29] Magnetic field assisted synthesis of Co2P hollow nanoparticles with controllable shell thickness for hydrogen evolution reaction
    Wang, Xiaoyang
    Liu, Chunhong
    Wu, Chun
    Tian, Xiaomin
    Wang, Kai
    Pei, Wenli
    Wang, Qiang
    ELECTROCHIMICA ACTA, 2020, 330
  • [30] Grass-like Co2P superstructures: direct synthesis between elements, forming mechanism and catalytic properties
    Wu, Hao
    Ni, Yonghong
    Hong, Feng
    Lu, Dican
    Xiao, Yanling
    RSC ADVANCES, 2016, 6 (07) : 5154 - 5160
12345