Creep-fatigue rupture mechanism and microstructure evolution around film-cooling holes in nickel-based DS superalloy specimen

被引：19
|
作者：
Zhao, Ting [1 ]
Hu, Xiaoan [1 ,2 ]
Jiang, Yun [2 ,3 ]
Teng, Xuefeng [1 ]
Liu, Fencheng [1 ]
Li, Bin [4 ]
Zhang, Shengliang [5 ]
Sun, Yantao [5 ]
机构：
[1] Nanchang Hangkong Univ, Sch Aircraft Engn, Nanchang 330063, Jiangxi, Peoples R China
[2] Nanchang Hangkong Univ, Jiangxi Key Lab Micro Aeroengine, Nanchang 330063, Jiangxi, Peoples R China
[3] Nanchang Hangkong Univ, Anal & Testing Ctr, Nanchang 330063, Jiangxi, Peoples R China
[4] China PLA Air Force, Equipment Dept, Beijing, Peoples R China
[5] Beijing Aeronaut Technol Res Ctr BATRC, Beijing, Peoples R China
来源：
INTERMETALLICS | 2021年 / 139卷
关键词：
Nickel-based superalloy; Creep-fatigue; Film-cooling hole; Fracture analyzation; Damage evolution; SINGLE-CRYSTAL SUPERALLOY; LIFE PREDICTION; BEHAVIOR; DAMAGE; DEFORMATION; FAILURE; STATE;
D O I：
10.1016/j.intermet.2021.107359
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
In this paper, creep-fatigue behaviors of the thin-walled tubular specimen with film holes were experimentally studied to address the influence of cyclic stress interruptions on creep strength and creep-fatigue life of a directionally solidified superalloy. The specimens with and without multiple holes were designed and manufactured to consider the effect of stress concentration produced by film cooling holes. The creep life of the specimen with holes has reduced significantly with the introduction of fatigue. An interesting result was found that the creep strength and life was enhanced on the stress concentrated specimens even if the creep loading was interruption by fatigue loadings, while creep fatigue life will be commonly shortened for notched specimen. Failure mechanisms related with cooling holes were analyzed on the basis of microscope observation.
引用
收藏
页数：9
相关论文
共 50 条
  • [41] Microstructure evolution and creep behavior of a [111] oriented single crystal nickel-based superalloy during tensile creep
    Yu, Huichen
    Su, Yong
    Tian, Ning
    Tian, Sugui
    Li, Ying
    Yu, Xingfu
    Yu, Lili
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 565 : 292 - 300
  • [42] Analysis of surface quality of multi-film cooling holes in nickel-based single crystal superalloy
    Wen, Z.
    Pei, H.
    Zhang, C.
    Wang, B.
    MATERIALS SCIENCE AND TECHNOLOGY, 2016, 32 (18) : 1845 - 1854
  • [43] High-temperature hot-corrosion effects on the creep-fatigue behavior of a directionally solidified nickel-based superalloy: Mechanism and lifetime prediction
    Li, Shaolin
    Yang, Xiaoguang
    Qi, Hongyu
    INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2020, 29 (05) : 798 - 809
  • [44] Revealing the influential mechanism of strain ranges on cyclic-life saturation during creep-fatigue in Nickel-based superalloy DZ445
    Ding, Biao
    Ren, Weili
    Zhong, Yunbo
    Yuan, Xiaotan
    Zheng, Tianxiang
    Shen, Zhe
    Guo, Yifeng
    Li, Qiang
    Peng, Jianchao
    Brnic, Josip
    Gao, Yanfei
    Liaw, Peter K.
    INTERNATIONAL JOURNAL OF PLASTICITY, 2022, 155
  • [45] Creep life analysis around film hole of nickel-based single crystal cooling blade
    Hou Naixian
    Yu Kuahai
    Yue Zhufeng
    RARE METAL MATERIALS AND ENGINEERING, 2008, 37 (04) : 625 - 628
  • [46] Numerical Simulation on the Creep Damage Evolution of Nickel-Based Single Crystal Specimens with Slant-Angled Film Cooling Holes
    Liang Jianwei
    Wen Zhixun
    Yue Zhufeng
    RARE METAL MATERIALS AND ENGINEERING, 2015, 44 (11) : 2656 - 2660
  • [47] Creep-fatigue interaction behavior of nickel-based single crystal superalloy at high temperature by in-situ SEM observation
    Wang, Zhen
    Wu, Wenwang
    Liang, Jiecun
    Li, Xide
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 141
  • [48] Numerical simulation on the creep damage evolution of nickel-based single crystal specimens with slant-angled film cooling holes
    Liang, Jianwei
    Wen, Zhixun
    Yue, Zhufeng
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2015, 44 (11): : 2656 - 2660
  • [49] Microstructure evolution of pre-compressi-on nickel-based single crystal superalloy during tensile creep
    Yu, Xingfu
    Tian, Sugui
    Du, Hongqiang
    Wang, Minggang
    Shang, Lijuan
    Cui, Shusen
    Jinshu Xuebao/Acta Metallurgica Sinica, 2008, 44 (08): : 961 - 967
  • [50] Effect of cooling rate during quenching on the microstructure and creep property of nickel-based superalloy FGH96
    Ye-fei Feng
    Xiao-ming Zhou
    Jin-wen Zou
    Gao-feng Tian
    InternationalJournalofMineralsMetallurgyandMaterials, 2019, 26 (04) : 493 - 499
12345