Synthesis and characterization of CrN/Mo2N multilayers and phases of Molybdenum nitride

被引：49

作者：

Koshy, Robin Abraham ^{[1
]}

Graham, Michael E. ^{[1
]}

Marks, Laurence D. ^{[1
]}

机构：

[1] Northwestern Univ, Dept Mat Sci & Engn, Evanston, IL 60208 USA

来源：

SURFACE & COATINGS TECHNOLOGY | 2007年 / 202卷 / 4-7期

基金：

美国国家科学基金会;

关键词：

lubricous oxides; multilayer coatings; CrN/Mo2N; in-situ lubrication; nanolayers; tool coatings;

D O I：

10.1016/j.surfcoat.2007.07.090

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

CrNx, MoNx, CrOx, MoOx and CrN/Mo2N multilayer films were deposited by reactive sputtering. Characterization of the coatings was carried out using XRD, XPS, optical profilometer, and nano-indentation. The oxidation of the thin films was studied as a function of annealing temperature. Tribological characterization of the Cr2O3 and the Mo-oxides was carried out as a function of annealing temperature. The low friction behavior of MoOx and MoNx was demonstrated. The deposition of CrNx and MoNx was also characterized and multilayer deposition of CrN and Mo2N was carried out. The hardness of Mo2N and CrN and the multilayers were shown to lie in the 20-30 GPa hardness regime. The multilayers are stable up to 500 degrees C in air and up to 1000 degrees C in argon. Initial friction testing on the multilayer coatings showed an activated self-lubricating mechanism. (c) 2007 Elsevier B.V. All rights reserved.

引用

页码：1123 / 1128

页数：6

共 28 条

[1] Self-lubrication mechanism via the in situ formed lubricious oxide tribofilm [J].

Aizawa, T ;

Mitsuo, A ;

Yamamoto, S ;

Sumitomo, T ;

Muraishi, S .

WEAR, 2005, 259 (1-6) :708-718

[2] Surface analysis of electrochemically stripped CrN coatings [J].

Conde, A. ;

Cristobal, A. B. ;

Fuentes, G. ;

Tate, T. ;

de Damborenea, J. .

SURFACE & COATINGS TECHNOLOGY, 2006, 201 (06) :3588-3595

[3] Preparation of ultralow-friction surface films on vanadium diboride [J].

Erdemir, A ;

Halter, M ;

Fenske, GR .

WEAR, 1997, 205 (1-2) :236-239

[4] High-temperature low-friction properties of vanadium-alloyed AlCrN coatings [J].

Franz, R. ;

Neidhardt, J. ;

Sartory, B. ;

Kaindl, R. ;

Tessadri, R. ;

Polcik, P. ;

Derflinger, V. H. ;

Mitterer, C. .

TRIBOLOGY LETTERS, 2006, 23 (02) :101-107

[5] A new low friction concept for high temperatures: lubricious oxide formation on sputtered VN coatings [J].

Gassner, G ;

Mayrhofer, PH ;

Kutschej, K ;

Mitterer, C ;

Kathrein, M .

TRIBOLOGY LETTERS, 2004, 17 (04) :751-756

[6] The effect of preferred orientation on the mechanical properties of chromium nitride coatings deposited on SKD11 by unbalanced magnetron sputtering [J].

Han, S ;

Lin, JH ;

Wang, GH ;

Shih, HC .

MATERIALS LETTERS, 2003, 57 (5-6) :1202-1209

[7]

HOFMANN S, 1990, WERKST KORROS, V41, P756

[8] Characterization of sputter-deposited chromium nitride thin films for hard coatings [J].

Hones, P ;

Sanjines, R ;

Levy, F .

SURFACE & COATINGS TECHNOLOGY, 1997, 94-5 (1-3) :398-402

[9] Structural and mechanical properties of chromium nitride, molybdenum nitride, and tungsten nitride thin films [J].

Hones, P ;

Martin, N ;

Regula, M ;

Lévy, F .

JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2003, 36 (08) :1023-1029

[10] Thermal stability of arc evaporated high aluminum-conteht Ti1-xAlxN thin films [J].

Hörling, A ;

Hultman, L ;

Odén, M ;

Sjölén, J ;

Karlsson, L .

JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 2002, 20 (05) :1815-1823

← 1 2 3 →