Re-crystallisation and interdiffusion in CGS/CIS bilayers

被引：19

作者：

Bodegård, M ^{[1
]}

Lundberg, O ^{[1
]}

Lu, J ^{[1
]}

Stolt, L ^{[1
]}

机构：

[1] Uppsala Univ, Angstrom Solar Ctr, S-75121 Uppsala, Sweden

来源：

THIN SOLID FILMS | 2003年 / 431卷

关键词：

CuInSe2; CuGaSe2; Cu(In; Ga)Se-2; interdiffusion; XRD;

D O I：

10.1016/S0040-6090(03)00252-9

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Stacked layers of CuGaSe2 and CuInSe2 grown in slightly Cu-rich conditions were compared to corresponding CuGaSe2 and CuInSe2 single layers using cross-section SEM and TEM analysis as well as XRD. All samples were grown both on Mo coated soda-lime glass substrates and on Mo coated glass substrates with an AI(2)O(3) barrier blocking Na outdiffusion. We found a difference in both grain structure and Ga-In interdiffusion behaviour depending on if Na was present or not during growth. In the Na-free case we found evidence of recrystallisation of the underlying CuGaSe2 layer during the subsequent CuInSe2 growth. In this case also the interdiffusion of In and Ga was enhanced as compared to the sample grown in the presence of Na. (C) 2003 Elsevier Science B.V. All rights reserved.

引用

页码：46 / 52

页数：7

共 6 条

[1] High voltage Cu(In,Ga)Se2 devices with Ga-profiling fabricated using co-evaporation
Bodegård, M
Lundberg, O
Malmström, J
Stolt, L
[J]. CONFERENCE RECORD OF THE TWENTY-EIGHTH IEEE PHOTOVOLTAIC SPECIALISTS CONFERENCE - 2000, 2000, : 450 - 453
[2] CULLITY BD, 1956, ELEMENTS XRAY DIFFRA, V1
[3] Influence of the Cu(In,Ga)Se2 thickness and Ga grading on solar cell performance
Lundberg, O
Bodegård, M
Malmström, J
Stolt, L
[J]. PROGRESS IN PHOTOVOLTAICS, 2003, 11 (02): : 77 - 88
[4] Marudachalam M., 1996, P 24 IEEE PHOT SPEC, P805
[5] Gallium diffusion and diffusivity in CuInSe2 epitaxial layers
Schroeder, DJ
Berry, GD
Rockett, AA
[J]. APPLIED PHYSICS LETTERS, 1996, 69 (26) : 4068 - 4070
[6] CRYSTAL-GROWTH AND DIFFUSION IN CU(IN, GA)SE2 CHALCOPYRITE THIN-FILMS
WALTER, T
SCHOCK, HW
[J]. THIN SOLID FILMS, 1993, 224 (01) : 74 - 81

← 1 →