Synthesis of Al2Cu intermetallic compound by mechanical alloying

被引:14
作者
Alam, Syed Nasimul [1 ]
Shrivastava, Pankaj [1 ]
Panda, Deepankar [1 ]
Gunale, Bhagavant [1 ]
Susmitha, Kunapuli [1 ]
Pola, Pridvuraj [1 ]
机构
[1] Natl Inst Technol Rourkela, Dept Met & Mat Engn, Rourkela 769008, Odisha, India
来源
MATERIALS TODAY COMMUNICATIONS | 2022年 / 31卷
关键词
Al2Cu; Mechanical Alloying (MA); HRTEM; Intermetallics; Rietveld analysis; AL-CU ALLOY; X-RAY; MATRIX COMPOSITES; COPPER; OXIDATION; TEMPERATURE; MICROSTRUCTURE; BEHAVIOR; PHASE; ROOM;
D O I
10.1016/j.mtcomm.2022.103267
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The alloy composition of Al-33.33 at% Cu (Al-54.15 wt% Cu) was selected for the present research. The effect of the milling duration on the synthesis of Al2Cu intermetallic compound was analyzed using several analytical techniques like XRD, SEM, EDX, HRTEM, and DSC/TGA. Nanostructured Al2Cu was successfully synthesized by mechanical alloying (MA) of Al-33.33 at% Cu powder for more than 15 h followed by annealing of the milled powder in Ar atmosphere at 1000 degrees C for 2 h. Residual Al and Cu powder that has not been transformed to Al2Cu were found in the milled powder even after 20 h of milling. Rietveld analysis was done for a better understanding of the phases evolved during MA and the annealing of the milled powders. The synthesis of the nanostructured intermetallic compound Al2Cu by MA followed by annealing of the milled powders was confirmed by analysis of the powders using various techniques.
引用
收藏
页数:12
相关论文
共 66 条
[1]   Mechanical milling of A1 and synthesis of in-situ Al2O3 particles by mechanical alloying of Al-CuO system [J].
Alam, Syed Nasimul ;
Sharma, Nidhi ;
Panda, Deepankar ;
Kumar, Abhishek ;
Sampenga, Dinesh ;
Sairam, Akella ;
Sarky, Vinod ;
Krupateja, M. B. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 753 :799-812
[2]   Nondestructive evaluation of mechanical properties of nanostructured Al-Cu alloy at room and elevated temperatures [J].
Ammar, Hany R. ;
Haggag, Fahmy M. .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2019, 29 (12) :2472-2482
[3]   In-situ analysis of incipient melting of Al2Cu in a novel high strength Al-Cu casting alloy using laser scanning confocal microscopy [J].
Andilab, Bernoulli ;
Ravindran, Comondore ;
Dogan, Neslihan ;
Lombardi, Anthony ;
Byczynski, Glenn .
MATERIALS CHARACTERIZATION, 2020, 159
[4]   Formation of Al2Cu and AlCu intermetallics in Al(Cu) alloy matrix composites by reaction sintering [J].
Aravind, M ;
Yu, P ;
Yau, MY ;
Ng, DHL .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 380 (1-2) :384-393
[5]   Synthesis and Characterization of Nanocrystalline Al-20 at. % Cu Powders Produced by Mechanical Alloying [J].
Ben Makhlouf, Molka ;
Bachaga, Tarek ;
Josep Sunol, Joan ;
Dammak, Mohamed ;
Khitouni, Mohamed .
METALS, 2016, 6 (07)
[6]  
Benjamin J.S., 1990, MET POWDER REPORT, V45, P122, DOI DOI 10.1016/S0026-0657(10)80124-9
[7]  
Cardoso K.R., INT LAT AM C POWD TE, V2001, P186
[8]   Effect of annealing on the interfacial structure of aluminum-copper joints [J].
Chen, Chih-Yuan ;
Hwang, Weng-Sing .
MATERIALS TRANSACTIONS, 2007, 48 (07) :1938-1947
[9]   Microstructure and Mechanical Properties of Nanocrystalline Al-Zn-Mg-Cu Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering [J].
Cheng, Jingfan ;
Cai, Qizhou ;
Zhao, Bingyi ;
Yang, Songfeng ;
Chen, Fei ;
Li, Bing .
MATERIALS, 2019, 12 (08)
[10]   X-ray diffraction investigation of the formation of nanostructured metastable phases during short-duration mechanical alloying of Cu-Al powder mixtures [J].
Chittineni, Kalyana ;
Bhat, Deepak G. .
MATERIALS AND MANUFACTURING PROCESSES, 2006, 21 (05) :527-533