Corrosion evolution and stress corrosion cracking of E690 steel for marine construction in artificial seawater under potentiostatic anodic polarization

被引：82

作者：

Lu, Qiankun ^{[2
]}

Wang, Liwei ^{[1
]}

Xin, Juncheng ^{[2
]}

Tian, Huiyun ^{[2
]}

Wang, Xin ^{[2
]}

Cui, Zhongyu ^{[2
]}

机构：

[1] Qingdao Univ, Coll Electromech Engn, Qingdao 266071, Peoples R China

[2] Ocean Univ China, Sch Mat Sci & Engn, Qingdao 266100, Peoples R China

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2020年 / 238卷

基金：

中国国家自然科学基金;

关键词：

Low alloy steel; Anodic polarization; Seawater; Pitting corrosion; Stress corrosion cracking; DUPLEX STAINLESS-STEEL; X70 PIPELINE STEEL; RARE-EARTH-ELEMENTS; HIGH-STRENGTH STEEL; LOW-ALLOY STEEL; CARBON-STEEL; PITTING CORROSION; WEATHERING STEEL; ATMOSPHERIC CORROSION; MECHANICAL-PROPERTIES;

D O I：

10.1016/j.conbuildmat.2019.117763

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In the present work, corrosion evolution and stress corrosion cracking behavior of E690 steel for marine equipment and construction under potentiostatic anodic polarization are investigated via electrochemical analysis, morphology and topography observation and slow strain rate tensile tests. Positive shift of anodic potential accelerates the two dissolution stages including electrochemical oxidation from Fe to Fe2+ and Fe2+ to Fe3+ of E690 steel. Composition of corrosion products is not altered by anodic polarization but the rust layer morphology and structure are changed. Pitting corrosion initiated around complex oxide inclusions and its transformation to uniform corrosion dominates the corrosion evolution process at OCP, while local acidification induced corrosion pits beneath thick and cracked rust layer dominates the localized corrosion under strong anodic polarization. The SCC susceptibility of E690 steel increases with the positive shift of applied anodic potentials, attributed to the acceleration of anodic dissolution (AD) effect under weak anodic polarization and synergistic effect of AD and hydrogen embrittlement (HE) under strong anodic polarization. (C) 2019 Elsevier Ltd. All rights reserved.

引用

页数：16

共 65 条

[1] The influence of microstructure on the protective properties of the corrosion product layer generated on the welded API X70 steel in chloride solution [J].

Alizadeh, Mostafa ;

Bordbar, Sajjad .

CORROSION SCIENCE, 2013, 70 :170-179

[2] Corrosion behavior of duplex stainless steel reinforcement in ternary binder concrete exposed to natural chloride penetration [J].

Alonso, M. C. ;

Luna, F. J. ;

Criado, M. .

CONSTRUCTION AND BUILDING MATERIALS, 2019, 199 :385-395

[3] In-depth distribution of rusts on a plain carbon steel and weathering steels exposed to coastal-industrial atmosphere for 17 years [J].

Asami, K ;

Kikuchi, M .

CORROSION SCIENCE, 2003, 45 (11) :2671-2688

[4] Atom probe field ion microscope measurements of carbon segregation at an α:α grain boundary and service failures by intergranular stress corrosion cracking [J].

Atrens, A ;

Wang, JQ ;

Stiller, K ;

Andren, HO .

CORROSION SCIENCE, 2006, 48 (01) :79-92

[5] Occluded solution chemistry control and the role of alloy sulfur on the initiation of crevice corrosion in type 304ss [J].

Brossia, CS ;

Kelly, RG .

CORROSION SCIENCE, 1998, 40 (11) :1851-1871

[6] Mechanical and environmental effects on stress corrosion cracking of low carbon pipeline steel in a soil solution [J].

Contreras, A. ;

Hernandez, S. L. ;

Orozco-Cruz, R. ;

Galvan-Martinez, R. .

MATERIALS & DESIGN, 2012, 35 :281-289

[7]

Corleto Carlos R., 2017, Case Studies in Engineering Failure Analysis, V9, P27, DOI 10.1016/j.csefa.2017.05.003

[8] Passivation behavior and surface chemistry of 2507 super duplex stainless steel in artificial seawater: Influence of dissolved oxygen and pH [J].

Cui, Zhongyu ;

Chen, Shuangshuai ;

Dou, Yunpeng ;

Han, Sike ;

Wang, Liwei ;

Man, Cheng ;

Wang, Xin ;

Chen, Shougang ;

Cheng, Y. Frank ;

Li, Xiaogang .

CORROSION SCIENCE, 2019, 150 :218-234

[9] Corrosion behavior of AZ31 magnesium alloy in the chloride solution containing ammonium nitrate [J].

Cui, Zhongyu ;

Ge, Feng ;

Lin, Yi ;

Wang, Liwei ;

Lei, Li ;

Tian, Huiyun ;

Yu, Mingdong ;

Wang, Xin .

ELECTROCHIMICA ACTA, 2018, 278 :421-437

[10] Passivation Behavior and Surface Chemistry of 2507 Super Duplex Stainless Steel in Acidified Artificial Seawater Containing Thiosulfate [J].

Cui, Zhongyu ;

Chen, Shuangshuai ;

Wang, Liwei ;

Man, Cheng ;

Liu, Zhiyong ;

Wu, Junsheng ;

Wang, Xin ;

Chen, Shougang ;

Li, Xiaogang .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2017, 164 (13) :C856-C868

← 1 2 3 4 5 6 7 →