Fretting wear properties of CrN and Cr2N coatings

被引：44
|
作者：
Tricoteaux, A [1 ]
Jouan, PY
Guerin, JD
Martinez, J
Djouadi, A
机构：
[1] Univ Valenciennes & Hainaut Cambresis, CRITT ZI Champ Abbesse, Lab Mat Avances Ceram, F-59600 Maubeuge, France
[2] Univ Valenciennes & Hainaut Cambresis Mont Houy, Lab Automat & Mecan Ind & Humaine, F-59313 Valenciennes 9, France
[3] ENSAM, Lab Bourguignon Mat & Procedes, F-71250 Cluny, France
来源：
SURFACE & COATINGS TECHNOLOGY | 2003年 / 174卷
关键词：
fretting wear properties; coatings; magnetron sputtering; CrN; Cr2N;
D O I：
10.1016/S0257-8972(03)00597-8
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Fretting wear experiments were carried out on CrN and Cr2N coatings. The chromium nitrides were deposited on 50 CrMo 4 steel substrate by reactive magnetron sputtering. The deposition conditions were optimised in order to obtain good adhesion and stoechiometric films. Scanning electron microscopy analyses were performed on the films. Fretting wear characterisations were conducted by using ball-on-flat geometries. By comparison with results obtained on the substrate, it was shown that fretting properties of Cr2N and CrN coatings are improved when grease lubricant is used in the mechanical contact. (C) 2003 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：440 / 443
页数：4
相关论文
共 50 条
  • [1] Monolithic and multilayer Cr/CrN, Cr/Cr2N, and Cr2N/CrN coatings on hard and soft substrates
    Kuruppu, M.L.
    Negrea, G.
    Ivanov, I.P.
    Rohde, S.L.
    Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films, 1998, 16 (3 pt 2):
  • [2] Monolithic and multilayer Cr/CrN, Cr/Cr2N, and Cr2N/CrN coatings on hard and soft substrates
    Kuruppu, ML
    Negrea, G
    Ivanov, IP
    Rohde, SL
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1998, 16 (03): : 1949 - 1955
  • [3] Growth and characterization of Cr2N/CrN multilayer coatings
    Aouadi, SM
    Schultze, DM
    Rohde, SL
    Wong, KC
    Mitchell, KAR
    SURFACE & COATINGS TECHNOLOGY, 2001, 140 (03): : 269 - 277
  • [4] Monolithic and multilayer Cr/CrN, Cr/Cr2N, and Cr 2N/CrN coatings on hard and soft substrates
    Department of Mechanical Engineering, University of Nebraska, Lincoln, NE 68588-0656, United States
    J. Vac. Sci. Technol. A Vac. Surf. Films, 3 (1949-1955):
  • [5] A comparative study of the oxidation behavior of Cr2N and CrN coatings
    Qi, Z. B.
    Liu, B.
    Wu, Z. T.
    Zhu, F. P.
    Wang, Z. C.
    Wu, C. H.
    THIN SOLID FILMS, 2013, 544 : 515 - 520
  • [6] Cr2N/CrN multilayer coatings for wood machining tools
    Warcholinski, B.
    Gilewicz, A.
    Ratajski, J.
    TRIBOLOGY INTERNATIONAL, 2011, 44 (09) : 1076 - 1082
  • [7] Microstructure and thermoelectric properties of CrN and CrN/Cr2N thin films
    Gharavi, M. A.
    Kerdsongpanya, S.
    Schmidt, S.
    Eriksson, F.
    Nong, N., V
    Lu, J.
    Balke, B.
    Fournier, D.
    Belliard, L.
    le Febvrier, A.
    Pallier, C.
    Eklund, P.
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2018, 51 (35)
  • [8] Insight into oxidation difference between Cr2N and CrN coatings
    Wu, Jiaojiao
    Shen, Mingli
    Wang, Wei
    Wang, Yanfeng
    Cheng, Yuxian
    Zhu, Shenglong
    SURFACES AND INTERFACES, 2024, 51
  • [9] Preparation of CrN/Cr2N multilayer coatings by unbalanced magnetron sputtering
    Zeng, XT
    Zhang, S
    Tan, BH
    Liu, YC
    SURFACE MODIFICATION TECHNOLOGIES X, 1997, : 899 - 908
  • [10] Fabrication of CrN/Cr2N bulk composites and their mechanical properties
    Aizawa, T
    Kuwahara, H
    Tamura, M
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2002, 85 (01) : 81 - 85
12345