Non-destructive prediction method of creep damage and remnant life related to those under creep-fatigue interactive conditions for nickel base superalloys

被引：2

作者：

Ando, A. ^{[1
]}

Yokobori, A. Toshimitsu, Jr. ^{[1
]}

Sugiura, R. ^{[1
]}

Ohmi, T. ^{[1
]}

Ozeki, G. ^{[1
]}

Matsubara, T. ^{[2
]}

机构：

[1] Tohoku Univ, Grad Sch Engn, Sendai, Miyagi 9808579, Japan

[2] Palmeso Co Ltd, Niigata, Japan

来源：

MATERIALS AT HIGH TEMPERATURES | 2015年 / 32卷 / 03期

关键词：

Nickel base superalloy; Non-destructive prediction; Creep damage; Remnant life; Microdamage; Micro slurry-jet erosion; CRACK-GROWTH RATE; HIGH-TEMPERATURE; Q-ASTERISK; PARAMETER; BEHAVIOR;

D O I：

10.1179/0960340914Z.00000000067

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In order to clarify the microdamage formation behaviour for high temperature brittle IN100 alloy, a polycrystalline nickel base superalloy, in situ observational test was carried out to observe creep damage formation behaviour of a notched IN100 specimen. Furthermore, the experimental findings of creep damage formation were evaluated by an original elastic-plastic creep finite element analysis. As a result, microcracks and damage forming areas were found to develop in the creep damage areas suggested by this analysis. This has resulted in the development of a non-destructive prediction method for creep damage accumulation and material's remnant life. The application of this method to the cases under creep-fatigue conditions was addressed.

引用

页码：266 / 275

页数：10

共 22 条

[11] Theoretical analysis of the effect of branched-cracks on the creep crack growth of advanced heat-resistant materials based on finite element method using a penalty function [J].

Takeuchi, Hiroaki ;

Yokobori, A. Toshimitsu, Jr. ;

Hosono, Shinji ;

Kobayashi, Daisuke ;

Sato, Koji .

JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2007, 71 (05) :452-457

[12]

Valluri S. R., 1984, P 6 INT C FRACT NEW, V3, P2181

[13]

Yamada Y., 1972, PLASTICITY VISCOELAS, P59

[14]

Yamamoto S., 2000, DEV HIGH TEMPERATURE

[15]

Yokbori Jr A. T., 2004, STRENGTH FRACT COMPL, V2, P35

[16]

Yokobori A. T. Jr., 2013, Strength, Fracture and Complexity, V8, P25, DOI 10.3233/SFC-130154

[17] Proposal of a new concept on creep fracture remnant life for a precracked specimen [J].

Yokobori, AT ;

Prager, M .

MATERIALS AT HIGH TEMPERATURES, 1999, 16 (03) :137-141

[18] AN ALTERNATIVE CORRELATING PARAMETER FOR CREEP CRACK-GROWTH RATE AND ITS APPLICATION - DERIVATION OF THE PARAMETER Q-ASTERISK [J].

YOKOBORI, AT ;

YOKOBORI, T ;

NISHIHARA, T ;

YAMAOKA, T .

MATERIALS AT HIGH TEMPERATURES, 1992, 10 (02) :108-118

[19] Estimation of creep crack growth rate in IN-100 based on the Q* parameter concept [J].

Yokobori, AT ;

Yokobori, T ;

Fuji, A ;

Kitagawa, M ;

Yamaya, I ;

Tabuchi, M ;

Yagi, K .

JOURNAL OF MATERIALS SCIENCE, 1998, 33 (06) :1555-1562

[20] Difference in the creep and creep crack growth behaviour between creep ductile and brittle materials [J].

Yokobori, AT .

ENGINEERING FRACTURE MECHANICS, 1999, 62 (01) :61-78

← 1 2 3 →