Environmentally assisted degradation spinodal copper alloy C72900

被引：22

作者：

Johnsen, Roy ^{[1
]}

Lange, Torstein ^{[2
]}

Stenerud, Gaute ^{[1
]}

Olsen, Jim Stian ^{[1
,3
]}

机构：

[1] Norwegian Univ Sci & Technol, Trondheim, Norway

[2] SINTEF, Trondheim, Norway

[3] Aker Solut, Fornebu, Norway

来源：

CORROSION SCIENCE | 2018年 / 142卷

关键词：

Copper; Hydrogen embrittlement; Stress corrosion; Sulfide cracking; Cathodic protection; De-alloying; CU-15NI-8SN ALLOY; DISCONTINUOUS PRECIPITATION; DECOMPOSITION;

D O I：

10.1016/j.corsci.2018.06.031

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this work, a spinodal Copper alloy - C72900, was tested to investigate the resistance against environmentally assisted degradation. The material was tested according to ISO 15156-3 Level V in sour H2S solution and to cathodic polarization in simulated seawater with stressed samples. The results showed no indications of hydrogen stress cracking under cathodic polarization in seawater. However, cracks up to 3 mm deep were found on the samples exposed to sour H2S environment. Energy Dispersive Spectroscopy showed severe depletion of copper close to the cracks which is associated with selective corrosion. Stress corrosion cracking was the dominating crack mechanism in the ISO 15156-3 Level V test.

引用

页码：45 / 55

页数：11

共 41 条

[1]

Al-Hajji J. N., 1993, CORROSION, V49

[2] On the discontinuous precipitation reaction and solute redistribution in a Cu-15%Ni-8%Sn alloy [J].

Alili, B. ;

Bradai, D. ;

Zieba, P. .

MATERIALS CHARACTERIZATION, 2008, 59 (10) :1526-1530

[3]

American Society for Testing and Materials (ASTM), D 1141: Standard Practice for the preparation of substitute Ocean Water

[4]

[Anonymous], 2008, F112 DNV RP

[5]

[Anonymous], 2015, B740092015 ASTM

[6]

[Anonymous], 2010, 21457 ISO

[7]

[Anonymous], TMO1981998 NACE

[8]

[Anonymous], TM01772005 NACE

[9]

[Anonymous], E11213 ASTM

[10]

[Anonymous], 1999, J AM I CONSERVATION, V38, P186

← 1 2 3 4 5 →