Effect of thermomechanical parameters on the critical strain for ultrafine ferrite formation through hot torsion testing

被引:79
作者
Beladi, H [1 ]
Kelly, GL [1 ]
Shokouhi, A [1 ]
Hodgson, PD [1 ]
机构
[1] Deakin Univ, Sch Engn & Technol, Geelong, Vic 3217, Australia
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2004年 / 367卷 / 1-2期
基金
澳大利亚研究理事会;
关键词
ultrafine ferrite; dynamic strain-induced transformation; hot torsion; critical strain;
D O I
10.1016/j.msea.2003.09.095
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A C-Mn-V steel was used to study ultrafine ferrite formation (1-3 mum) through dynamic strain-induced transformation (DSIT) using hot torsion experiments. A systematic study determined the critical strain for the start of DSIT (epsilon(C,DSIT)), although this may not lead to a fully ultrafine microstructure. Therefore, the strain to produce an ultrafine ferrite (UFF) as final microstructure (epsilon(C,UFF)) during deformation was also determined. In addition, the effect of thermomechanical parameters such as deformation temperature, prior austenite grain size, strain rate and cooling rate on epsilon(C,DSIT) and epsilon(C,UFF) has been evaluated. DSIT ferrite nucleated on prior austenite grain boundaries at an early stage of straining followed by intragranular nucleation at higher strains. The prior austenite grain size affected the distribution of DSlT ferrite nucleation sites at an early stage of transformation and the subsequent coarsening behaviour of the grain boundary and intragranular ferrite grains during post-deformation cooling. Also, epsilon(C,DSIT) and epsilon(C,UFF) increased with an increase in the prior austenite grain size and deformation temperature. The post-deformation cooling had a strong effect not only on epsilon(C,UFF) but also the UFF microstructure (i.e. final ferrite grain size and second phase characteristics). (C) 2003 Elsevier B.V. All rights reserved.
引用
收藏
页码:152 / 161
页数:10
相关论文
共 25 条
[1]  
ADACHI Y, 2001, INT S ULTR GRAIN STE, P84
[2]  
BELADI H, IN PRESS MAT SCI TEC
[3]   Microstructural evolution during the austenite-to-ferrite transformation from deformed austenite [J].
Bengochea, R ;
Lopez, B ;
Gutierrez, I .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (02) :417-426
[4]   Influence of the prior austenite microstructure on the transformation products obtained for C-Mn-Nb steels after continuous cooling [J].
Bengochea, R ;
López, B ;
Gutierrez, I .
ISIJ INTERNATIONAL, 1999, 39 (06) :583-591
[5]  
Beynon J. H., 1992, Materials Forum, V16, P37
[6]  
CHOO WY, 2001, INT S ULTR GRAIN STE, P2
[7]   The effect of plastic deformation of austenite on the kinetics of subsequent ferrite formation [J].
Hanlon, DN ;
Sietsma, J ;
van der Zwaag, S .
ISIJ INTERNATIONAL, 2001, 41 (09) :1028-1036
[8]   The effect of chemistry on the formation of ultrafine ferrite in steel [J].
Hickson, MR ;
Russell, RK ;
Hodgson, PD .
ISIJ INTERNATIONAL, 1999, 39 (11) :1176-1180
[9]  
HODGSON PD, 1992, THESIS U QUEENSLAND
[10]  
HODGSON PD, 1997, INT S PHYS SIM, P219