The Effect of Viscosity and Application Mode of Phosphoric Acid on Bond Strength of GlassFiber Post

Background: When a phosphoric acid is used, before applying an adhesive system, it is known that obtaining an effective adhesion to the root canal walls is a challenge. The aim of the present study was to evaluate the influence of phosphoric acid viscosity and application mode on the push-out bond strength (BS) values of fiberglass post to root dentin. The conditioning pattern on the root dentin was also evaluated. Materials and Methods: The roots of 44 endodontically treated premolars were divided into 4 groups, of eleven teeth each, according to the combination of the main factors: phosphoric acid viscosity (liquid or gel) and application mode (passive or sonic). After application of the two-step etch-and-rinse adhesive system, the fiberglass posts were cemented with a dual-cure resin-cement. Roots were sectioned transversely into six 1-mm slices for push-out BS test at 0.5 mm/min Some roots of each group were selected for evaluation of the conditioning pattern by scanning electron microscopy. BS results (three-way ANOVA and Tukey's test) and the conditioning pattern (Kruskal-Wallis test and Mann-Whitney test) were statistically evaluated (alpha = 0.05). Results: The highest BS value was observed with a liquid phosphoric acid under sonic application mode (p < 0.05), being all other groups similar to one another (p < 0.05). Also, the highest BS value was observed in the cervical third, followed by the medium and the apical thirds (p < 0.05). The sonic application produced better smear layer removal and opening of dentinal tubules for both viscosities (p = 0.015). Conclusion: A better bonding of fiberglass posts to root canals can be achieved when the post spaces are conditioned with a liquid phosphoric acid under sonic application.