Effects of correlative factors on the interdendritic melt flow brought by the bulge in continuous casting slabs

被引：4
作者：
Chen, Shuying [1 ,2 ]
Chan, Guowei [2 ]
Wang, Jianzhong [2 ]
Wu, Chunjing [1 ]
机构：
[1] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
[2] Liaoning Inst Technol, Dept Mat & Chem Engn, Jinzhou 121001, Peoples R China
来源：
JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING | 2008年 / 15卷 / 04期
基金：
中国国家自然科学基金;
关键词：
continuous casting; two-phase region; melt flow; macrosegregation;
D O I：
10.1016/S1005-8850(08)60077-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of various factors on the flow speed of interdendritic melt were analyzed in detail in the process of continuous casting slabs. When the solid-liquid interface bends periodically, the expression of solute distribution in the columnar crystal zone was deduced, and the quantitative calculation was also made. The results show that the bulge and the interdendritic spacing. are responsible for the flow speed of interdendritic melt. At the initial stage of solidification the bulge operates, and at the final stage the interdendritic spacing operates. The experimental results of macro segregation in the slabs validated the calculated results of the flow speed of interdendritic melt, which shows that the calculated results are basically consistent with the experimental ones. (c) 2008 University of Science and Technology Beijing. All rights reserved.
引用
收藏
页码：407 / 411
页数：5
相关论文
共 16 条
  • [1] [曹海峰 CAO Haifeng], 2005, [材料研究学报, Chinese Journal of Materials Research], V19, P594
  • [2] Chang GW, 2001, T NONFERR METAL SOC, V11, P708
  • [3] CONG M, 2002, CASTING HDB CAST STE, P34
  • [4] FUJII H, 1978, T IRON STEEL I JPN, V18, P510
  • [5] Han ZQ, 2003, ACTA METALL SIN, V39, P140
  • [6] HU HQ, 1991, SOLIDIFICATION PRINC, P214
  • [7] JIE WQ, 1994, METALL MATER TRANS B, V25, P731, DOI 10.1007/BF02655181
  • [8] Kusano A, 1998, TETSU TO HAGANE, V84, P43
  • [9] MAENO S, 1984, T ISIJ, V24, P83
  • [10] Miyazawa K., 1979, IRONMAK STEELMAK, V6, P68
12