Interfacial investigation of in situ oxidation of 4H-SiC

被引：63
|
作者：
Virojanadara, C [1 ]
Johansson, LI [1 ]
机构：
[1] Linkoping Univ, Dept Phys, S-58183 Linkoping, Sweden
来源：
SURFACE SCIENCE | 2001年 / 472卷 / 1-2期
关键词：
semi-conductor-insulator interfaces; silicon carbide; oxidation; silicon oxides;
D O I：
10.1016/S0039-6028(00)00967-5
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
An in situ oxidation study of root3 x root3 R30 degrees reconstructed 4H-SiC(0001) surfaces is reported. An intermediate oxidation state (interpreted to be Si+1) is revealed in core level photoemission spectra recorded from the in situ prepared SiO2/4H-SiC samples. Oxidation was made at a pressure of similar to 10(-3) Torr in flowing oxygen and at substrate temperatures from 600 degreesC to 950 degreesC. The highest oxidation rate was obtained at 800 degreesC when approximate to 25 Angstrom thick SiO2 layers were prepared. The surface related C 1s components observed on the clean reconstructed 4H-SiC(0001) surfaces were found to disappear after oxidation. No carbon or carbon containing by-product at the interface or in the oxide were possible to observe for the films grown. (C) 2001 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：L145 / L149
页数：5
相关论文
共 50 条
  • [21] Pore Wall Thinning of Mesoporous 4H-SiC by Sacrificial Oxidation
    Rashid, Marzaini
    Idris, Muhammad Idzdihar
    Horrocks, Benjamin Richard
    Healy, Noel
    Goss, Jonathan Paul
    Horsfall, Alton Barrett
    CRYSTAL RESEARCH AND TECHNOLOGY, 2018, 53 (09)
  • [22] Controlled thermal oxidation of sacrificial silicon on 4H-SiC epilayer
    Koh, A
    Kestle, A
    Dunstan, PR
    Pritchard, M
    Wilks, SP
    Pope, G
    Mawby, PA
    SILICON CARBIDE AND RELATED MATERIALS - 1999 PTS, 1 & 2, 2000, 338-3 : 1081 - 1084
  • [23] Enhancing oxidation rate of 4H-SiC by oxygen ion implantation
    Liu, Min
    Zhang, Shuyuan
    Yang, Xiang
    Chen, Xue
    Fan, Zhongchao
    Wang, Xiaodong
    Yang, Fuhua
    Ma, Chao
    He, Zhi
    JOURNAL OF MATERIALS SCIENCE, 2019, 54 (02) : 1147 - 1152
  • [24] Comparison of thermal oxidation and plasma oxidation of 4H-SiC (0001) for surface flattening
    Deng, Hui
    Endo, Katsuyoshi
    Yamamura, Kazuya
    APPLIED PHYSICS LETTERS, 2014, 104 (10)
  • [25] Effect of the oxidation process on SiO2/4H-SiC interface electrical characteristics
    Palmieri, R.
    Boudinov, H.
    Radtke, C.
    da Silva, E. F., Jr.
    APPLIED SURFACE SCIENCE, 2008, 255 (03) : 706 - 708
  • [26] Scratching properties of 4H-SiC single crystal after oxidation under different conditions
    Ban, Xinxing
    Tian, Zhuangzhi
    Zheng, Shaodong
    Zhu, Jianhui
    Ba, Wenlan
    Wang, Ningchang
    Han, Shaoxing
    Qiu, Hui
    Wang, Xing
    Li, Zhengxin
    WEAR, 2024, 556
  • [27] An investigation of thin Zn films on 4H-SiC(0001)-graphene
    Idczak, K.
    Wachowicz, E.
    Prochnicka, A.
    Markowski, L.
    Tringides, M. C.
    APPLIED SURFACE SCIENCE, 2019, 487 : 1348 - 1355
  • [28] Experimental Investigation on Ablation of 4H-SiC by Infrared Femtosecond Laser
    Wang, Lukang
    Zhao, You
    Yang, Yu
    Zhang, Manman
    Zhao, Yulong
    MICROMACHINES, 2022, 13 (08)
  • [29] Investigation of stacking faults introduced into 4H-SiC crystals by indentation
    Orlov V.I.
    Yakimov E.B.
    Journal of Surface Investigation: X-ray, Synchrotron and Neutron Techniques, 2017, 11 (1) : 234 - 237
  • [30] Selective growth of 4H-SIC on 4H-SiC substrates using a high temperature mask
    Li, C
    Seiler, J
    Bhat, I
    Chow, TP
    SILICON CARBIDE AND RELATED MATERIALS 2003, PTS 1 AND 2, 2004, 457-460 : 185 - 188
12345