In the present study, fly ash-based pervious concrete (FPC) is fabricated using sintered fly ash aggregates. Materials used include OPC Type I cement, the coarse aggregate of size 4.75, 9.5, 12.5 mm, water, and superplasticiser. Using these materials, various concrete mixtures were developed with a water to cement ratio of 0.30, 0.35, and 0.40, respectively. The effect of these parameters on the mechanical properties of the pervious concrete such as compressive strength, flexural strength, tensile strength, permeability, porosity, abrasion resistance, and leachability is studied. The test results showed that pervious concrete materials made with sintered fly ash aggregates had a better mechanical as compared to natural available aggregate. In addition, the concrete with SFA aggregates could achieve compressive strength ranges from 7.15 to 17.40 MPa with porosity range from 26.79 to 34.05% and these can be adopted as an environment-friendly concrete.