Wear Behavior of Basalt Filled Low Density Polyethylene Composites

被引:44
作者
Akinci, Akin [1 ]
Yilmaz, Senol [1 ,2 ]
Sen, Ugur [1 ]
机构
[1] Sakarya Univ, Fac Engn, Dept Met & Mat Engn, TR-54187 Sakarya, Turkey
[2] Tubitak MAM, Mat Inst, Gebze, Kocaeli, Turkey
关键词
Low density polyethylene; Basalt; Friction; Wears; LDPE FILMS; GLASS; POLYMERS; FRICTION; CRYSTALLIZATION; POLYPROPYLENE; ADHESION; PLASMA;
D O I
10.1007/s10443-011-9208-9
中图分类号
TB33 [复合材料];
学科分类号
摘要
The friction and wear performance of pure LDPE and 10%, 30%, 50% and 70% basalt filled (by wt) LDPE composite were comparatively evaluated under dry sliding conditions. Wear tests were carried out at room temperature under 5, 10 and 20N loads and at 0.5, 1.0 and 1.5 m/s sliding speeds. The coefficients of friction of the composites were significantly influenced with increase in basalt content. Friction coefficient of the LDPE was getting decreased from 0.51 to 0.13 with increase in basalt content, depending on applied loads and sliding speeds. The results show that the wear rates for pure LDPE and basalt filled composites increase with increasing loads and sliding speeds. The wear rates of the basalt filled composites were significantly affected from the basalt content. Wear rates of the LDPE was decreased from 2.596 x 10(-3) to 6.8 x 10(-5) mm(3)/m with increase in basalt content, depending on applied loads and sliding speeds.
引用
收藏
页码:499 / 511
页数:13
相关论文
共 21 条
[11]   Chain architecture of LDPE as a function of molar mass using size exclusion chromatography and multi-angle laser light scattering (SEC-MALLS) [J].
Tackx, P ;
Tacx, JCJF .
POLYMER, 1998, 39 (14) :3109-3113
[12]   Dry sliding performance of thermoplastics against reinforced unsaturated polyester (BMC): In use in electrical contact breakers components [J].
Unal, H. ;
Mimaroglu, A. ;
Serdar, V. .
WEAR, 2006, 261 (7-8) :841-847
[13]   Abrasive wear behaviour of polymeric materials [J].
Unal, H ;
Sen, U ;
Mimaroglu, A .
MATERIALS & DESIGN, 2005, 26 (08) :705-710
[14]   Dry sliding wear characteristics of some industrial polymers against steel counterface [J].
Unal, H ;
Sen, U ;
Mimaroglu, A .
TRIBOLOGY INTERNATIONAL, 2004, 37 (09) :727-732
[15]   Wear behavior of a glass fiber-reinforced PEI composite [J].
Vina, J. ;
Garcia, M. A. ;
Castrillo, M. A. ;
Vina, I. ;
Arguelles, A. .
JOURNAL OF THERMOPLASTIC COMPOSITE MATERIALS, 2008, 21 (03) :279-286
[16]   Sliding wear behavior and mechanism of ultra-high molecular weight polyethylene [J].
Wang, YQ ;
Li, J .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 266 (1-2) :155-160
[17]   Internal friction studies of particulate filled polypropylene [J].
Weidenfeller, B. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 442 (1-2) :371-374
[18]   Organic-inorganic hybrid sol-gel materials .2. Application for dental composites [J].
Yang, JM ;
Chen, HS ;
Hsu, YG ;
Lin, FH ;
Chang, YH .
ANGEWANDTE MAKROMOLEKULARE CHEMIE, 1997, 251 :61-72
[19]   Crystallization kinetics of basalt glass [J].
Yilmaz, S ;
Ozkan, OT ;
Gunay, V .
CERAMICS INTERNATIONAL, 1996, 22 (06) :477-481
[20]   Preparation, stabilization and characterization of TiO2 on thin polyethylene films (LDPE).: Photocatalytic applications [J].
Yu Zhiyong ;
Mielczarski, E. ;
Mielczarski, J. ;
Laub, D. ;
Buffat, Ph. ;
Klehm, U. ;
Albers, P. ;
Lee, K. ;
Kulik, A. ;
Kiwi-Minsker, L. ;
Renken, A. ;
Kiwi, J. .
WATER RESEARCH, 2007, 41 (04) :862-874