The high-speed deformation behavior of TRIP steels

The high-speed deformation behavior of TRIP steel was investigated at strain rates ranging from 10(-2) s(-1) to 10(3)s(-1). The effects of metallurgical factors, such as the rolling direction, thickness, and gage length, on the tensile properties at various strain rates were evaluated. The ultimate tensile strength, uniform elongation, strain rate sensitivity, absorbed energy, and strain-hardening exponent are reported. In general, the strength increases and the ductility decreases as the strain rate increases. The samples with a high amount of retained austenite had two distinct regions of strain rate sensitivity, showing high strain rate sensitivity over a strain rate of 10(2) s(-1). The tensile properties were not affected by the gage length and thickness of the tensile samples; however, the rolling direction of the tensile samples affected the UTS values slightly. The absorbed energy of the TRIP steel greatly exceeded that of HSLA steel.