Effect of vibratory weld conditioning on valve residual stress and fracture toughness

被引：0

作者：

Lu, Qinghua ^{[1
]}

Chen, Ligong ^{[1
]}

Ni, Chunzhen ^{[1
]}

机构：

[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Shanghai 200030, Peoples R China

来源：

PROCEEDINGS OF THE INTERNATIONAL CONFERENCE ON MECHANICAL ENGINEERING AND MECHANICS 2007, VOLS 1 AND 2 | 2007年

关键词：

vibratory weld conditioning; residual stress; fracture toughness;

D O I：

暂无

中图分类号：

TP [自动化技术、计算机技术];

学科分类号：

0812 ;

摘要：

In the present work the effects of vibratory weld conditioning (VWC) on residual stress and fracture toughness of full welded valve have been investigated. The experiment results show that vibration reduces residual deformation and stress generally. Fracture test is carried out using single edge notch bend (SENB) specimens. The fracture surfaces of failed weld metal (WM) specimens are characterized by dimple-like structures. The depth and density of these dimples increase with vibration applied in welding. While the fracture characteristic of the heat-affected zone (HAZ) is river marking, indicating brittle fracture mode. The possible solidification behaviour in VWC is discussed in this paper.

引用

页码：1044 / 1048

页数：5

共 50 条

[41] Effect of residual stress on brittle fracture testing [J].

Hill, MR ;

Panontin, TL .

FATIGUE AND FRACTURE MECHANICS: TWENTY-NINTH VOLUME, 1999, 1332 :154-175

[42] Influence of weld joint mechanical properties on fracture toughness [J].

Gliha, V ;

Rak, I ;

Gubeljak, N ;

Kocak, M .

ADVANCES IN FRACTURE RESEARCH, VOLS 1-6, 1997, :531-538

[43] Effect of Post Weld Heat Treatment on Microstructure and Fracture Toughness of Friction Welded Joint [J].

Wu Sujun ;

Han Bo ;

Zhao Dalong ;

Ji Yingping ;

Shao Ling .

JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2016, 31 (06) :1347-1351

[44] Effect of post weld heat treatment on microstructure and fracture toughness of friction welded joint [J].

Sujun Wu ;

Bo Han ;

Dalong Zhao ;

Yingping Ji ;

Ling Shao .

Journal of Wuhan University of Technology-Mater. Sci. Ed., 2016, 31 :1347-1351

[45] Effect of Post Weld Heat Treatment on Microstructure and Fracture Toughness of Friction Welded Joint [J].

吴素君 ;

HAN Bo ;

ZHAO Dalong ;

JI Yingping ;

SHAO Ling .

JournalofWuhanUniversityofTechnology(MaterialsScience), 2016, 31 (06) :1347-1351

[46] Evaluation of microhardness, fracture toughness and residual stress in a thermal barrier coating system: A modified Vickers indentation technique [J].

Mao, W. G. ;

Wan, J. ;

Dai, C. Y. ;

Ding, J. ;

Zhang, Y. ;

Zhou, Y. C. ;

Lu, C. .

SURFACE & COATINGS TECHNOLOGY, 2012, 206 (21) :4455-4461

[47] Evaluation of fracture toughness through the modeling of indentation residual stress field and crack shape [J].

Lee, YH ;

Kwon, D .

SCIENCE OF ENGINEERING CERAMICS II, 1999, 2 :569-572

[48] Effects of PWHT on the impact toughness and fracture toughness of the weld metal under restraint welding [J].

Wang D. ;

Liu K. ;

Deng C. ;

Gong B. ;

Wu S. ;

Xiao N. .

Hanjie Xuebao/Transactions of the China Welding Institution, 2020, 41 (08) :63-67and78

[49] Effect of hygrothermal conditioning on the fracture toughness of carbon/epoxy composites cured in autoclave/Quickstep [J].

Khan, Laraib Alam ;

Mahmood, Ali Hasan ;

Syed, Ahmed Shuja ;

Khan, Zaffar M. ;

Day, Richard J. .

JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2013, 32 (16) :1165-1176

[50] Effect of Thermal Aging on SCC, Material Properties and Fracture Toughness of Stainless Steel Weld Metals [J].

Lucas, T. ;

Ballinger, R. G. ;

Hanninen, H. ;

Saukkonen, T. .

15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, :883-900

← 1 2 3 4 5 →