Edge cracking due to a compressive residual stress in ceramic laminates

被引：10
作者：
Leguillon, Dominique [1 ]
Sevecek, Oldrich [2 ]
Martin, Eric [3 ]
Bermejo, Raul [4 ]
机构：
[1] Univ Paris 06, Sorbonne Univ, Inst Jean Le Rond dAlembert, CNRS UMR 7190, F-75005 Paris, France
[2] Brno Univ Technol, Fac Mech Engn, Inst Solid Mech Mechatron & Biomech, Brno 61669, Czech Republic
[3] Univ Bordeaux, Lab Composites Thermostruct, CNRS UMR 5801, F-33600 Pessac, France
[4] Univ Leoben, Inst Struktur & Funkt Skeram, A-8700 Leoben, Austria
来源：
COMPTES RENDUS MECANIQUE | 2015年 / 343卷 / 03期
关键词：
Ceramic laminates; Residual stresses; Fracture mechanics; Coupled criterion; POROUS INTERLAYERS; LAYERED CERAMICS; TOUGHNESS; STRENGTH; COMPOSITES; DEFLECTION; FAILURE; DESIGN;
D O I：
10.1016/j.crme.2014.11.001
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The onset of an edge crack in compressive layers of a ceramic laminate undergoing residual stresses is predicted using the stress-energy coupled criterion based on the data of the tensile strength and the toughness of the material under consideration. The proposed criterion does not contain any adjustable parameter, which is its indisputable advantage. The results of predictions of the edge crack nucleation are in a very good agreement with the experimental observations of this phenomenon. They allow us to recover and even to improve slightly an approximate formula to estimate the critical layer thickness as a function of the compressive residual stress that was proposed some years ago. (C) 2014 Academie des sciences. Published by Elsevier Masson SAS. All rights reserved.
引用
收藏
页码：192 / 198
页数：7
相关论文
共 50 条
[41]   Residual stress and thermal expansion of graphite epoxy laminates subjected to cryogenic temperatures [J].
Ifju, Peter ;
Myers, Donald ;
Schulz, William .
COMPOSITES SCIENCE AND TECHNOLOGY, 2006, 66 (14) :2449-2455
[42]   Evaluation of the Compressive Residual Stress Relaxation Behavior by in situ X-ray Stress Measurement [J].
Hayama, Motoaki ;
Kikuchi, Shoichi ;
Komotori, Jun .
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2021, 107 (02) :137-145
[43]   Evaluation of the Compressive Residual Stress Relaxation Behavior by in situ X-ray Stress Measurement [J].
Hayama, Motoaki ;
Kikuchi, Shoichi ;
Komotori, Jun .
ISIJ INTERNATIONAL, 2022, 62 (04) :758-765
[44]   Modeling on temperature-dependent first matrix cracking stress for fiber reinforced ceramics considering fiber debonding and residual thermal stress [J].
Deng, Yong ;
Li, Weiguo ;
Zhang, Xuyao ;
Li, Ying ;
Kou, Haibo ;
Shao, Jiaxing ;
Zhang, Xianhe ;
Qu, Zhaoliang .
CERAMICS INTERNATIONAL, 2018, 44 (17) :21666-21674
[45]   The effects of residual stress on the non-linear behaviour of composite laminates Part I. Experimental results and residual-stress assessments [J].
Perreux, D ;
Lazuardi, D .
COMPOSITES SCIENCE AND TECHNOLOGY, 2001, 61 (02) :167-175
[46]   Thermal residual stress analysis of epoxy bi-material laminates and bonded joints [J].
Jumbo, F. S. ;
Ashcroft, I. A. ;
Crocombe, A. D. ;
Wahab, M. M. Abdel .
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2010, 30 (07) :523-538
[47]   Finite element reliability analysis of edge delamination onset due to interlaminar stresses in composite laminates [J].
Delbariani-Nejad, Ali ;
Farrokhabadi, Amin ;
Fotouhi, Mohammad .
COMPOSITE STRUCTURES, 2022, 288
[48]   The microstructure model on the residual stress distribution of metal-ceramic coating [J].
Ji, Jing ;
Zhou, Jianqiu ;
Pang, Xuming ;
Dong, Shuhong ;
Hu, Ruiqin ;
Hu, Aosheng .
COMPUTATIONAL MATERIALS SCIENCE, 2014, 85 :332-339
[49]   Free-Edge Interlaminar Stress Analysis of Composite Laminates Using Interface Modeling [J].
Kim, Heung Soo ;
Lee, Jaehun ;
Cho, Maenghyo .
JOURNAL OF ENGINEERING MECHANICS, 2012, 138 (08) :973-983
[50]   Experimental and three-dimensional numerical investigation of matrix cracking and delamination interaction with edge effect of curved composite laminates [J].
Cao, Dongfeng ;
Hu, Haixiao ;
Duan, Qingfeng ;
Song, Peihao ;
Li, Shuxin .
COMPOSITE STRUCTURES, 2019, 225
12345