An experimental study of iron corrosion in sulfuric acid solution containing inhibitors by noise measurement

被引：4
|
作者：
Meszaros, L
Meszaros, G
Pirnat, A
Lengyel, B
机构：
[1] Laboratory for Inorganic Chemistry, Hungarian Academy of Sciences, H-1112 Budapest
来源：
JOURNAL OF THE ELECTROCHEMICAL SOCIETY | 1996年 / 143卷 / 11期
关键词：
D O I：
10.1149/1.1837258
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
The corrosion of pure iron was studied by electrochemical noise potential measurements in 0.5 mol/dm(3) H2SO4 containing dibenzyl sulfoxide and plenyl thiourea, respectively, as the inhibitor. The corrosion current density was found to be inversely proportional to the mean square of the potential noise. The proportionality constant was determined with solution analysis and harmonic analysis.
引用
收藏
页码：3597 / 3600
页数：4
相关论文
共 50 条
  • [41] Evaluation of some bipyridinium dihalides as inhibitors for low carbon steel corrosion in sulfuric acid solution
    Chemistry Department, Faculty of Science, Assiut University, 71516 Assiut, Egypt
    不详
    不详
    Journal of Applied Electrochemistry, 2008, 38 (09): : 1301 - 1311
  • [42] Phenothiazine drugs as novel and eco-friendly corrosion inhibitors for copper in sulfuric acid solution
    Zhou, Ling
    Zhang, Shengtao
    Tan, Bochuan
    Feng, Li
    Xiang, Bin
    Chen, Feng
    Li, Weining
    Xiong, Bingxue
    Song, Tingting
    JOURNAL OF THE TAIWAN INSTITUTE OF CHEMICAL ENGINEERS, 2020, 113 : 253 - 263
  • [43] EFFECT OF VELOCITY AND OXYGEN ON CORROSION OF IRON IN SULFURIC ACID
    FOROULIS, ZA
    UHLIG, HH
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1964, 111 (01) : 13 - 17
  • [44] STUDIES ON ALTERNATING-CURRENT CORROSION OF IRON .2. CORROSION OF IRON IN A SULFURIC-ACID SOLUTION BY ALTERNATING-CURRENT
    TORIGOE, Y
    DENKI KAGAKU, 1977, 45 (08): : 518 - 522
  • [45] CORROSION-ELECTROCHEMICAL BEHAVIOR OF TERNARY ALLOYS OF IRON, CHROMIUM AND NICKEL IN THE SULFURIC ACID SOLUTION
    Shirinov, T. I.
    Tagirli, G. M.
    Guseynov, M. Ch.
    Mamedova, R. R.
    CHEMICAL PROBLEMS, 2016, (02): : 180 - 185
  • [46] In situ STM study of Cu(111) surface structure and corrosion in pure and benzotriazole-containing sulfuric acid solution
    Polewska, W
    Vogt, MR
    Magnussen, OM
    Behm, RJ
    JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (47): : 10440 - 10451
  • [47] THE CORROSION BEHAVIOR OF STAINLESS-STEEL IN AQUEOUS ETHANOL SOLUTION CONTAINING SULFURIC-ACID
    SEKINE, I
    YUASA, M
    KOHARA, K
    CORROSION SCIENCE, 1990, 31 : 579 - 584
  • [48] CORROSION WEAR OF DUPLEX STAINLESS-STEELS IN SULFURIC-ACID-SOLUTION CONTAINING CHLORIDE
    ZHANG, TC
    JIANG, XX
    LU, XC
    LI, SZ
    SHI, CX
    CORROSION, 1994, 50 (05) : 339 - 344
  • [49] Comparative study on the corrosion behavior of low alloy steels in sulfuric acid solution
    LI Yongcan
    LIANG Gaofei
    YAN Yuanyuan
    Baosteel Technical Research, 2016, 10 (04) : 3 - 11
  • [50] Corrosion of mortars in sulfuric acid and sodium sulfate solution
    Key Laboratory of Advanced Civil Engineering Materials, Tongji University, Shanghai 200092, China
    Jianzhu Cailiao Xuebao, 2006, 6 (724-728):
12345