RETRACTED: Highly Active Rare-Earth-Metal La-Doped Photocatalysts: Fabrication, Characterization, and Their Photocatalytic Activity (Retracted Article)

被引:51
作者
Anandan, S. [1 ,2 ]
Ikuma, Y. [2 ]
Murugesan, V. [1 ]
机构
[1] Anna Univ, Dept Chem, Madras 600025, Tamil Nadu, India
[2] Kanagawa Inst Technol, Dept Appl Chem, Atsugi, Kanagawa 2430292, Japan
关键词
EU3+ IONS; TIO2; NANOPARTICLES; PERSISTENT; DEGRADATION; OXIDATION; CATALYSTS; ACID;
D O I
10.1155/2012/921412
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Efficient La-doped TiO2 photocatalysts were prepared by sol-gel method and extensively characterized by various sophisticated techniques. The photocatalytic activity of La-doped TiO2 was evaluated for the degradation of monocrotophos (MCPs) in aqueous solution. It showed higher rate of degradation than pure TiO2 for the light of wavelength of 254 nm and 365 nm. The rate constant of TiO2 increases with increasing La loading and exhibits maximum rate for 1% La loading. The photocatalytic activities of La-doped TiO2 are compared with La-doped ZnO; the reaction rate of the former is similar to 1.8 and 1.1 orders higher than the latter for the lights of wavelength 254 nm and 365 nm, respectively. The relative photonic efficiency of La-doped TiO2 is relatively higher than La-doped ZnO and commercial photocatalysts. Overall, La-doped TiO2 is the most active photocatalyst and shows high relative photonic efficiencies and high photocatalytic activity for the degradation of MCP. The enhanced photocatalytic activity of La-doped TiO2 is mainly due to the electron trapping by lanthanum metal ions, small particle size, large surface area, and high surface roughness of the photocatalysts.
引用
收藏
页数:10
相关论文
共 41 条
[41]   Direct splitting of water under visible light irradiation with an oxide semiconductor photocatalyst [J].
Zou, ZG ;
Ye, JH ;
Sayama, K ;
Arakawa, H .
NATURE, 2001, 414 (6864) :625-627