Redox Equilibrium of Niobium in Calcium Silicate Base Melts

被引：4

作者：

Mirzayousef-Jadid, A-M. ^{[1
]}

Schwerdtfeger, Klaus ^{[1
]}

机构：

[1] Tech Univ Clausthal, Inst Met, D-38678 Clausthal Zellerfeld, Germany

来源：

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE | 2010年 / 41卷 / 05期

关键词：

CARBON-SATURATED IRON; PARTITION; VANADIUM; SLAGS; MN; NB;

D O I：

10.1007/s11663-010-9386-0

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The oxidation state of niobium has been determined at 1873 K(1600 degrees C) in CaO-SiO(2)-NbO(x) melts with CaO/SiO(2) ratios (mass pct) of 0.66, 0.93 and 1.10, and 5.72 to 11.44 pct Nb(2)O(5) (initial). The slag samples were equilibrated with gas phases of controlled oxygen pressure, then quenched to room temperature and analyzed chemically. The niobium is mainly pentavalent with small amounts in the tetravalent state. It was found that the Nb(5+)/Nb(4+) ratio increases with oxygen pressure at a constant CaO/SiO(2) ratio and constant content of total niobium, closely according to the ideal law of mass action, which is proportional to p(O2)(1/4). The ratio also increases with total niobium content, and it seems to have a maximum at a basicity of about 0.93. The color of the solidified slag samples is described and is explained with the help of transmission spectra.

引用

页码：1038 / 1041

页数：4

共 18 条

[1] ELECTROCHEMICAL STUDIES OF MONOMERIC NIOBIUM(V) AND NIOBIUM(IV) PORPHYRINS IN NONAQUEOUS MEDIA [J].

ANDERSON, JE ;

LIU, YH ;

GUILARD, R ;

BARBE, JM ;

KADISH, KM .

INORGANIC CHEMISTRY, 1986, 25 (21) :3786-3791

[2]

BARIN I, 1989, THERMOCHEMICAL DAT 2

[3]

Bonnet KD, 2001, IRONM CONF PROC, V60, P1223

[4]

Brookins D.G., 1988, EH PH DIAGRAMS GEOCH

[5]

Cotton F A., 1967, Anorganische Chemie

[6]

INOUE R, 1987, T IRON STEEL I JPN, V27, P946

[7]

INOUE R, 1983, TETSU TO HAGANE, V69, P1129

[8]

MASSALSKI TD, 1986, BINARY ALLOY PHASE D, V2, P1683

[9] Redox Equilibria of Chromium in Calcium Silicate Base Melts [J].

Mirzayousef-Jadid, A. -M. ;

Schwerdtfeger, Klaus .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2009, 40 (04) :533-543

[10]

MIRZAYOUSEFJADI.AM, 2001, THESIS TU CLAUSTHAL

← 1 2 →