Experimental Analysis and Damage Modeling of High-Density Polyethylene under Fatigue Loading

被引：17

作者：

Djebli, A. ^{[1
]}

Bendouba, M. ^{[1
]}

Aid, A. ^{[1
]}

Talha, A. ^{[2
,3
]}

Benseddiq, N. ^{[2
]}

Benguediab, M. ^{[4
]}

机构：

[1] Univ Mustapha Stambouli, Fac Sci & Technol, LPQ3M, Mascara, Algeria

[2] Univ Lille 1, LML, Dept Genie Mecan, F-59655 Villeneuve Dascq, France

[3] Ecole Hautes Etud Ingn, HEI, Paris, France

[4] Univ Sidi Bel Abess, Fac Technol, Sidi Bel Abbes, Algeria

来源：

ACTA MECHANICA SOLIDA SINICA | 2016年 / 29卷 / 02期

关键词：

HDPE; semi-crystalline; damage accumulation; stiffness degradation; CRACK-PROPAGATION; ALUMINUM-ALLOY; BEHAVIOR; FRACTURE; ACCUMULATION; PREDICTION; MECHANICS; FAILURE; POLYMER; TENSILE;

D O I：

10.1016/S0894-9166(16)30102-1

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this study, an experimental analysis for determining the fatigue strength of HDPE-100 under cyclic loading is presented. The curve of cumulative fatigue damage versus number of cycles (D-N) was deduced from stiffness degradation. Based on the three stage damage trend, the remaining fatigue life is numerically predicted by considering a double term power damage accumulation model. This model is found to be accurate, both in modeling the rapid damage growth in the early life and near the end of the fatigue life. Numerical results illustrate that the proposed model is capable of accurately fitting several different sets of experimental data.

引用

页码：133 / 144

页数：12

共 49 条

[11] Experimental investigations and modeling of volume change induced by void growth in polyamide 11 [J].

Boisot, G. ;

Laiarinandrasana, L. ;

Besson, J. ;

Fond, C. ;

Hochstetter, G. .

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2011, 48 (19) :2642-2654

[12] A nonlinear CDM model for ductile failure [J].

Bonora, N .

ENGINEERING FRACTURE MECHANICS, 1997, 58 (1-2) :11-28

[13] FATIGUE CRACK-GROWTH IN POLYETHYLENE [J].

BUCKNALL, CB ;

DUMPLETON, P .

POLYMER ENGINEERING AND SCIENCE, 1985, 25 (06) :313-317

[14] Cavitation in strained polyvinylidene fluoride: mechanical and X-ray experimental studies [J].

Castagnet, S ;

Girault, S ;

Gacougnolle, JL ;

Dang, P .

POLYMER, 2000, 41 (20) :7523-7530

[15] Experimental and numerical characterization of damage evolution in steels [J].

Celentano, Diego J. ;

Chaboche, Jean-Louis .

INTERNATIONAL JOURNAL OF PLASTICITY, 2007, 23 (10-11) :1739-1762

[16] A NON-LINEAR CONTINUOUS FATIGUE DAMAGE MODEL [J].

CHABOCHE, JL ;

LESNE, PM .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1988, 11 (01) :1-17

[17] CONTINUUM DAMAGE MECHANICS .1. GENERAL CONCEPTS [J].

CHABOCHE, JL .

JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1988, 55 (01) :59-64

[18] Influence of joining on the fatigue and fracture behavior of high density polyethylene pipe [J].

Chen, H ;

Scavuzzo, RJ ;

Srivatsan, TS .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1997, 6 (04) :473-480

[19] Improvement of forging process of a 3D complex part with respect to damage occurrence [J].

Cherouat, A ;

Saanouni, K ;

Hammi, Y .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 142 (02) :307-317

[20] A non-linear energy model of fatigue damage accumulation and its verification for Al-2024 aluminum alloy [J].

Djebli, A. ;

Aid, A. ;

Bendouba, M. ;

Amrouche, A. ;

Benguediab, M. ;

Benseddiq, N. .

INTERNATIONAL JOURNAL OF NON-LINEAR MECHANICS, 2013, 51 :145-151

← 1 2 3 4 5 →