3-D Surface Morphological Characterization of CAD/CAM Milled Dental Zirconia: An In Vitro Study of the Effect of Post-Fabrication Processes

Objective: To investigate the effect on zirconia surface of the post-fabrication surface treatments on the morphological characteristics and mechanical properties of CAD/CAM milled dental zirconia specimens as well as to identify the critical parameters in the measurement of oral retention under in vitro circumstances. Method: The zirconia specimens (N = 20, n = 4) were subjected to CAD/CAM milling and divided into five groups. The specifications were: Group G1-sintered; Group G2-sintered followed by a polishing process; Group G3-sintered followed by polishing and sandblasting with alumina particles Al2O3 (110 mu m); Group G4-sintered followed by sandblasting; Group G5-sintered followed by sandblasting with polishing as the end process. All the groups were subjected to Fretting wear tests, 3-D surface roughness measurements, and Vickers's Micro hardness tests. Investigation of the phase transformation using XRD, and surface feature examination using SEM were also carried out. Additionally, one-way ANOVA, Tukey, and Pearson correlations were statistically analysed. Results: The fabrication processes had a significant effect on the performance of zirconia specimens in all the groups (p > 0.05). Specimens that underwent polishing as the last process exhibited lower surface roughness. The monoclinic phase of zirconia was observed in all the specimens before and after wear except for those in the G2 and G5 groups, where polishing was the end process. In G5, the post-wear surface properties revealed lower surface roughness and hardness. Further, the SEM and 3-D topography show grooves as seen by the dale void volume (Vvv) values; shallow valley depth (Svk); micro craters; and wear track. Conclusion: Specimens in G5 that were subjected to multistep post-fabrication process, namely sandblasting followed by polishing, yielded better results when compared to those in the other groups (G1, G2, G3, and G4). G5 with an interlayer of alumina is recommended for clinical applications due to its enhanced surface properties, mechanical properties, and low wear.