Effects of molybdenum on precipitation behaviours in aged cast stainless steels

The effects of Mo on precipitation behaviours in aged cast stainless steels have been investigated. Mo-free CF3 steel and Mo-bearing CF3M steel, both of which consisted of a duplex structure of ferrite and austenite phases, were prepared. Microstructural evolution in the ferrite phase during ageing at 723K has been observed by transmission electron microscopy (TEM). Precipitates in CF3 steel were identified to belong to the G-phase and possess lattice coherency with the ferrite phase at interphase boundaries. On the other hand, precipitates in CF3M steel were found to be nanodomains of not only to the G-phase but also to another phase enriched in Mo. Some of the nanodomains containing Mo exhibited diffraction patterns having pseudo five-fold symmetry, but others exhibited regular periodicity in high-resolution TEM images. The atomic structure of the Mo-related nanodomains is proposed to be a distorted -phase that retains coherency with the matrix.